Preparation and characterization of highly transparent epoxy/inorganic nanoparticle hybrid thin films

doi:10.1016/j.tsf.2013.05.038

淡江大學機構典藏 > 工學院 > 化學工程與材料工程學系暨研究所 > 期刊論文 > Item 987654321/96932

請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/96932

題名:	Preparation and characterization of highly transparent epoxy/inorganic nanoparticle hybrid thin films
作者:	Yu, Yang-Yen;Rao, Yu-Cyuan;Chang, Chao-Ching
貢獻者:	淡江大學化學工程與材料工程學系
關鍵詞:	Epoxy-titania hybrid materials;High transparent films;Thermal polymerization;Refractive index;Sol–gel method
日期:	2013-11-01
上傳時間:	2014-03-14 13:08:13 (UTC+8)
出版者:	Lausanne: Elsevier S.A.
摘要:	This paper presents the preparation of epoxy/inorganic-nanoparticle hybrid materials synthesized from diglycidyl ether of bisphenol A and colloidal titania (TiO2) with coupling agent, 3-isocyanatopropyltriethoxysilane, and curing agent, hexahydro-4-methylphthalic anhydride, by using a thermal polymerization. The precursor was spin-coated and thermal-cured to form hybrid films. The experimental results showed that the refractive index of hybrid films can be tuned by adding various solid contents of TiO2 to hybrid films. The refractive index at 633 nm increased from 1.450 to 1.639 as the TiO2 content increased from 0 to 50 wt.%. UV–vis analysis showed that the transparency of hybrid films was over 90%. L.a.b. color analysis indicated that the luminance of films was above 95%, and no yellowing was observed. In addition, the hybrid materials exhibited a low hydroscopic property under a high-humidity environment.
關聯:	Thin Solid Films 546, pp.236–241
DOI:	10.1016/j.tsf.2013.05.038
顯示於類別:	[化學工程與材料工程學系暨研究所] 期刊論文

文件中的檔案:

檔案	大小	格式	瀏覽次數
index.html	0Kb	HTML	267	檢視/開啟
index.html	0Kb	HTML	201	檢視/開啟
TSF+546-236.pdf	660Kb	Adobe PDF	366	檢視/開啟

在機構典藏中所有的資料項目都受到原著作權保護.

TAIR相關文章

資料載入中.....