    題名: Preparation and Sensor Application of Carbon Coated Zinc Oxide Nanorods Array
    作者: Chung, Ren-Jei;Wang, Huey-Yuan;Li, Yu-Ching;Yeh, Ping-Hung
    貢獻者: 淡江大學物理學系
    關鍵詞: Zinc oxide nanorod arrays;Carbon;Hydrothermal process;Chemical vapor deposition;Sensing devices;Schottky contact
    日期: 2013
    上傳時間: 2014-03-07 11:16:26 (UTC+8)
    摘要: In this study, zinc oxide (ZnO) nanorod arrays (NRAs) coated with carbon material were fabricated onto a silicon substrate through a hydrothermal method followed by chemical vapor deposition. A series of tests were carried out, including crystallinity analysis, microstructure observation and investigation of the luminescent and electrical properties. We further constructed a nanosensing device for UV light and carbon monoxide (CO) through fabrication of a Schottky contact. The sensing abilities of the zinc oxide NRA devices before and after carbon coating were compared. The sensing mechanism was also investigated. The results indicated that the carbon coating was amorphous, with high mechanical strength, specific light transmittance and high resistance to chemical corrosion. After coating with carbon, the zinc oxide nanorods retained their original structure. In the UV light sensing test, the carbon layer retarded the electron transport, but the carbon-coated NRA device showed a higher average current in response to UV light compared to the bare NRA device. In the CO sensing experiment, the carbon coating provided functional groups for CO adsorption and improved the sensitivity.
    關聯: Journal of the Australian Ceramics Society 49(2), pp.81-88
    顯示於類別:[物理學系暨研究所] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    index.html0KbHTML173檢視/開啟
    index.html館藏資訊0KbHTML144檢視/開啟
    index.html0KbHTML133檢視/開啟

    在機構典藏中所有的資料項目都受到原著作權保護.

    TAIR相關文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - 回饋