題名:	Tribological Analysis of Copper-Coated Graphite Particle-Reinforced A359 Al/5 wt.% SiC Composites
作者:	Lin, C.B.;Wang, T.C.;Chang, Z.C.;Chu, H.Y.
貢獻者:	淡江大學機械與機電工程學系
關鍵詞:	aluminum matrix composites;graphite;silicon carbide;wear
日期:	2013-01-01
上傳時間:	2014-02-20 16:59:24 (UTC+8)
出版者:	Springer
摘要:	Copper-coated graphite particles can be mass-produced by the cementation process using simple equipment. Graphite particulates that were coated with electroless copper and 5 wt.% SiC particulates were introduced into an aluminum alloy by compocasting to make A359 Al/5 wt.% SiC(p) composite that contained 2, 4, 6, and 8 wt.% graphite particulate composite. The effects of SiC particles, quantity of graphite particles, normal loading, sliding speed and wear debris on the coefficient of friction, and the wear rate were investigated. The results thus obtained indicate that the wear properties were improved by adding small amounts of SiC and graphite particles into the A359 Al alloy. The coefficient of friction of the A359 Al/5 wt.% SiC(p) composite that contained 6.0 wt.% graphite particulates was reduced to 0.246 and the amount of graphite film that was released on the worn surface increased with the graphite particulate content. The coefficient of friction and the wear rate were insensitive to the variation in the sliding speed and normal loading.
關聯:	Journal of Materials Engineering and Performance 22(1), pp.94-103
DOI:	10.1007/s11665-012-0231-2
顯示於類別:	[機械與機電工程學系暨研究所] 期刊論文

文件中的檔案:

檔案	描述	大小	格式	瀏覽次數
1059-9495_22(1)p94-103.pdf		1390Kb	Adobe PDF	363	檢視/開啟
index.html		0Kb	HTML	264	檢視/開啟

在機構典藏中所有的資料項目都受到原著作權保護.

TAIR相關文章

資料載入中.....