自由基架構硬化之PU樹脂探討

淡江大學機構典藏 > 理學院 > 化學學系暨研究所 > 會議論文 > Item 987654321/95016

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/95016

题名:	自由基架構硬化之PU樹脂探討
作者:	林文欽;陳幹男
贡献者:	淡江大學化學學系
关键词:	聚胺基甲酸酯;光起始劑;樹脂;熱處理;自由基;Polyurethane;Photo-Initiator;Resin;Heat Treatment;Free Radical
日期:	1992-06
上传时间:	2014-02-09 07:34:06 (UTC+8)
摘要:	自由基架橋硬化的PU樹脂,由聚酯多元醇和過量的甲苯二異氰酸酯進行加成反應,得PU預聚合物,然後再加入2-羥烯酸酯反應得末端基具有不飽和雙鍵的PU寡聚合物,此樹脂加入熱及光起始劑,產生自由基架橋硬化。本文合成不同成分的PU樹脂,並探討了各種反應稀釋劑的量,和填充劑的量或摻入耦合劑,對PU樹脂所造成的影響,其結果利用萬能拉力機、硬度計、黏度計、示差掃描卡計、電子顯微鏡等方式來評估結果。 Free-radical curable PU resins were prepared from the reactions of polyols with excess toluene diisocyanates, and then 2-hydroxyethyl methacrylate was introduced into these PU prepolymers as the terminal groups. A thermal initiator and a photo-initiator were added into these prepared PU resins. They became both thermal and UV curable oligomers. For the case of TiO was added as a filler for these PU oligomers. A coupling agent was added in order to improve the viscosity and the binding between the filler and PU resins. They were cured both with thermal treatments and UV radiations. The physical and mechanical properties of cured PU films were evaluated with tensile strength, durometer, viscometer, DSC, TGA, SEM and etc...
關聯:	第十五屆高分子研討會論文專集第八卷第一冊=Proceedings of the 15th ROC Polymer Symposium 1992 (I)
显示于类别:	[化學學系暨研究所] 會議論文

文件中的档案:

档案	描述	大小	格式	浏览次数
自由基架構硬化之PU樹脂探討_英文摘要.docx	摘要	17Kb	Microsoft Word	120	检视/开启
自由基架構硬化之PU樹脂探討＿中文摘要.docx	摘要	15Kb	Microsoft Word	227	检视/开启

在機構典藏中所有的数据项都受到原著作权保护.

TAIR相关文章

数据加载中.....