BaFe/sub 12/O/sub 19/ Powder Preparation by Pyrolyzing the Corresponding Ester Precursors

淡江大學機構典藏 > 工學院 > 化學工程與材料工程學系暨研究所 > 會議論文 > Item 987654321/94974

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/94974

题名:	BaFe/sub 12/O/sub 19/ Powder Preparation by Pyrolyzing the Corresponding Ester Precursors
作者:	Yu, Husan-Fu;Huang, Kuo-Chao
贡献者:	淡江大學化學工程學系
关键词:	前驅物法;粉體製備;酯;Precursor Method;Powder Preparation;Ester
日期:	1999-11
上传时间:	2014-02-09 00:50:29 (UTC+8)
摘要:	Magnetic BaFe/sub 12/O/sub 19/ with ultrafine crystallites was produced via a citric acid precursor method. Ester precursors that contained the required amount of Ba/sub 2+/ and Fe/sub 3+/ to form barium ferrites were prepared by chelating Ba/sub 2+/ and Fe/sub 3+/ with citric acid in an aqueous solution of nitrates and then reacting the solution with ethylene glycol at 353 K. The pH values of aqueous solutions were adjusted using ammonium hydroxide. The dried solid precursors were then pyrolyzed at 623, 873 and 1,073 K, respectively. The effects of pH of the starting aqueous solutions on the characteristics of the resultant powder were studied using SEM, TEM, EDM, XRD, and EDS. The experimental results showed that the powder obtained at 873 K or below was composed of .gamma.-Fe/sub 2/ O/sub 3/ and BaCO/sub 3/. At 1,073 K, submicron crystalline BaFe/sub 12/O/sub 19/ powder was obtained.
關聯:	八十八年度化工學會年會及研討會專輯─化學工程技術研討會論文集
显示于类别:	[化學工程與材料工程學系暨研究所] 會議論文

文件中的档案:

档案	大小	格式	浏览次数
BaFe／sub 12／O／sub 19／ Powder Preparation by Pyrolyzing the Corresponding Ester Precursors_英文摘要.docx	18Kb	Microsoft Word	192	检视/开启

在機構典藏中所有的数据项都受到原著作权保护.

TAIR相关文章