Fabrication of flexible conductive films derived from poly(3,4-ethylenedioxythiophene)–poly(styrenesulfonic acid) (PEDOT:PSS) on the nonwoven fabrics substrate

doi:10.1016/j.matchemphys.2013.08.037

淡江大學機構典藏 > 工學院 > 化學工程與材料工程學系暨研究所 > 期刊論文 > Item 987654321/93289

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/93289

题名:	Fabrication of flexible conductive films derived from poly(3,4-ethylenedioxythiophene)–poly(styrenesulfonic acid) (PEDOT:PSS) on the nonwoven fabrics substrate
作者:	Wu, Chieh-Han;Shen, Hsiu-Ping;Don, Trong-Ming;Chiu, Wen-Yen
贡献者:	淡江大學化學工程與材料工程學系
关键词:	Composite materials;Electrical conductivity;Coatings;Elastic properties
日期:	2013-12-16
上传时间:	2013-12-16 09:48:16 (UTC+8)
出版者:	Elsevier S.A.
摘要:	In this research, conducting poly(3,4-ethylenedioxythiophene)–poly(styrenesulfonic acid) (PEDOT:PSS) aqueous dispersion was synthesized at first via chemical oxidative polymerization and followed by mixing it with poly(styrene-r-butyl acrylate) P(St-BA) aqueous latex, creating a conductive material with outstanding stretchability. The elastic conductive composite were then film formed on the glass and poly(ethylene terephthalate) (PET) nonwoven fabric substrate by spin coating and dip coating, respectively. Composite films with various contents of PEDOT:PSS polymer (10–100 wt.%) had been prepared. From the conductivity measurements, the conductivity was still kept as high as 88 S cm−1 even the PEDOT:PSS content was lowered to 10 wt.%. Furthermore, the elasticity of conductive films on the PET-nonwoven fabric substrate was evaluated by the 180° bending test repeating 100 times. With introducing soft P(St-BA) material in the PEDOT:PSS phase, the surface resistance increased merely 3–6 times after bending 100 times, while the surface resistance for pure PEDOT:PSS film could reach 18–20 times.
關聯:	Materials Chemistry and Physics 143(1), pp.143-148
DOI:	10.1016/j.matchemphys.2013.08.037
显示于类别:	[化學工程與材料工程學系暨研究所] 期刊論文

文件中的档案:

档案	描述	大小	格式	浏览次数
index.html		0Kb	HTML	135	检视/开启

在機構典藏中所有的数据项都受到原著作权保护.

TAIR相关文章

数据加载中.....