    題名: Flame retardation behaviors of UV-curable phosphorus-containing PU coating system
    作者: Wang, Shih-Chieh;Chen, Po-Chen;Hwang, Jing-Zhong;Huang, Chi-Yuan;Yeh, Jen-Taut;Chen, Kan-Nan
    貢獻者: 淡江大學化學學系
    淡江大學化學工程與材料工程學系
    關鍵詞: flame retardation;nano-silica;phosphonic acid;PU;UV-curing
    日期: 2013-11
    上傳時間: 2013-10-19 14:29:07 (UTC+8)
    摘要: A UV-cured polyurethane (PU)/nano-silica composite with a flame-retarded coating system was obtained from the composition of nano-silica containing a UV-curable PU oligomer and a UV-reactive phosphonic acid [ethylene glycol methacrylate phosphate (EGMP)]. The UV-curable PU oligomer was prepared by an addition reaction of 2-hydroxyethyl methacrylate (2-HEMA) with an NCO-terminated PU pre-polymer; this was then mixed with a methanol dispersion of nano-silica. The UV-reactive phosphonic acid (EGMP) was prepared by a reaction of 2-HEMA with phosphorus pentoxide (P2O5). The curing reaction of the PU/nano-silica composite coating system was carried out by UV irradiation with the aid of a photoinitiator (2-hydroxy-2-methylpropiophenone). The thermal properties of these PU/nano-silica composite coatings were investigated by the measurements of dynamic mechanical analysis (DMA) and thermogravimetric analysis (TGA), respectively. A phosphorus (phosphonic acid) containing ingredient, EGMP in PU coating system that provides good adhesion to steel surface and flame retardation. Their physical properties (contact angle, hardness) and flame flammability [limiting oxygen index (LOI), UL-94 test] with various phosphorus contents (different dosages of EGMP) were also evaluated in this report.
    關聯: Journal of Polymer Engineering 33(8), pp.749-756
    DOI: 10.1515/polyeng-2013-0136
    顯示於類別:[化學學系暨研究所] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    index.html0KbHTML53檢視/開啟

    在機構典藏中所有的資料項目都受到原著作權保護.

    TAIR相關文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - 回饋