Preparation and characterization of polymer/zirconia nanocomposite antistatic coatings on plastic substrates

doi:10.1007/s11998-012-9427-5

淡江大學機構典藏 > 工學院 > 化學工程與材料工程學系暨研究所 > 期刊論文 > Item 987654321/92541

請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/92541

題名:	Preparation and characterization of polymer/zirconia nanocomposite antistatic coatings on plastic substrates
作者:	Chang, Chao-Ching;Hwang, Feng-His;Hsieh, Chin-Yuan;Chen, Ching-Chung;Cheng, Liao-Ping
貢獻者:	淡江大學化學工程與材料工程學系淡江大學能源與光電材料研究中心
關鍵詞:	Zirconia;Antistatic;UV-curing;Acrylate resin;Hardness
日期:	2013-01
上傳時間:	2013-10-17 17:37:26 (UTC+8)
出版者:	New York: Springer New York LLC
摘要:	Zirconia nanoparticles synthesized by the sol–gel method were surface modified by the coupling agent, 3-(trimethoxy silyl) propyl methacrylate (MSMA), containing C=C bonds. These particles were then UV-cured together with the hexa-functional monomer, dipentaethritol hexaacrylate (DPHA), to prepare transparent coatings that exhibited antistatic property on plastic substrates. FTIR and solid 29SiNMR were used to analyze the chemical bonds in the formed particles and coatings. Dynamic light scattering measurement of the modified ZrO2 sol indicated a relatively small particle size distribution, 1.5–20 nm, with a maximum intensity at ~5.5 nm. These particles dispersed uniformly in the organic host, poly(DPHA), as was manifested by the high resolution SEM images of the coatings. Antistatic performance of the coatings was examined based on the surface resistivity measurements. A resistivity of 7.74 × 108 Ω/□ suited to common antistatic applications could be attained for coatings containing 10% inorganic component. In addition, all of the prepared coatings were very hard with pencil hardness 7H–8H, and they attached perfectly to the PMMA substrate according to the peel test.
關聯:	Journal of Coatings Technology and Research 10(1), pp.73-78
DOI:	10.1007/s11998-012-9427-5
顯示於類別:	[化學工程與材料工程學系暨研究所] 期刊論文