Effects of argon plasma treatment on the adhesion property of ultra high molecular weight polyethylene (UHMWPE) textile

淡江大學機構典藏 > 工學院 > 化學工程與材料工程學系暨研究所 > 期刊論文 > Item 987654321/92482

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/92482

题名:	Effects of argon plasma treatment on the adhesion property of ultra high molecular weight polyethylene (UHMWPE) textile
作者:	Huang, Chi-Yuan;Wu, Jing-Yi;Tasi, Chin-Shan;Hsieh, Kuo-Huang;Yeh, Jen-Taut;Chen, Kan-Nan
贡献者:	淡江大學化學學系
关键词:	UHMWPE;Surface modification;Adhesive;Peel strength
日期:	2013-09
上传时间:	2013-10-16 13:00:59 (UTC+8)
出版者:	Lausanne: Elsevier S.A.
摘要:	In this investigation, effects of argon plasma on surface modification of ultra high molecular weight polyethylene (UHMWPE) textile were studied. After argon plasma treatment, the peeling test of UHMWPE textile/adhesive (PU_T01) composites were measured by ISO 10339:2003 and then observed the morpho-surface composites by SEM analysis. In addition, the contact angle of UHMWPE textile by argon plasma was also measured. Results showed that the peel strength of UHMWPE textile/adhesive (PU_T01) composites was increased from 0.6 kgf/in to 4.6 kgf/in as argon plasma treatment with treated power of 40 W and treated time of 5 min. From SEM observation, the surface of UHMWPE textile was introduced the number of anchors after argon plasma treatment. After plasma treatment, the UHMWPE react with adhesive. And the contact angle on surface of UHMWPE textile was decreased from 80° to 28°.
關聯:	Surface & Coatings Technology 231(25), pp.507–511