The effect of dislocations on crack propagation in wrinkled gold film deposited on polydimethylsiloxane

淡江大學機構典藏 > 工學院 > 機械與機電工程學系暨研究所 > 期刊論文 > Item 987654321/90569

請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/90569

題名:	The effect of dislocations on crack propagation in wrinkled gold film deposited on polydimethylsiloxane
作者:	Lin, C. B.;Lin, C. C.;Lee, Sanboh;Chou, Y. T.
貢獻者:	淡江大學機械與機電工程學系
關鍵詞:	cracks;dislocations;fracture;gold;metallic thin films
日期:	2008
上傳時間:	2013-06-27 15:48:33 (UTC+8)
出版者:	College Park: American Institute of Physics
摘要:	Crack propagation in a wrinkled thin film of gold deposited on polydimethylsiloxane (PDMS) was affected by the presence of folding defects—the ripple dislocations. The ripple pattern, ripple dislocations, and the crack were simultaneously formed after the tensile load applied on the PDMS substrate was removed. The crack, however, was unstable and propagated forward. The propagation rate increased when the crack passed by the ripple dislocations, but less significantly when it advanced near a ripple dislocation dipole. Such crack dislocation interaction implies that the ripple dislocation has an internal stress field. The measured data of the rate process were analyzed based on the theory of fracture mechanics, and an empirical relationship between the crack velocity and the crack extension force was presented.
關聯:	Journal of Applied Physics 104(1), 016106(3pages)