Contactless molding of arrayed chalcogenide glass lenses

doi:10.1016/j.jnoncrysol.2010.11.077

淡江大學機構典藏 > 工學院 > 機械與機電工程學系暨研究所 > 期刊論文 > Item 987654321/89053

請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/89053

題名:	Contactless molding of arrayed chalcogenide glass lenses
作者:	Ma, Kung Jeng;Chien, Hsi Hsin;Huang, Su Wei;Fu, Wen Yen;Chao, Choung-Lii
貢獻者:	淡江大學機械與機電工程學系
關鍵詞:	Contactless molding;Arrayed lenses;Chalcogenide glass;Viscoelastic deformation
日期:	2011-06
上傳時間:	2013-05-08 13:50:03 (UTC+8)
出版者:	Amsterdam: Elsevier BV * North-Holland
摘要:	The moldable chalcogenide glass material has been developed recently. This study developed a new process to produce an arrayed chalcogenide glass lenses by a contactless molding process, which is considered to have a great potential for the mass production of arrayed glass lenses with low cost, ease of manufacture and free of surface defects. The stainless steel plate with arrayed through holes was employed as the molds. The selenium based chalcogenide glass plate was put on the mold and nitrogen gas was introduced into the closed chamber to allow gas pressure up to 4 kg/cm2. IR heating allows the chalcogenide glass plate to approach the soft point, and forces glass flows into the arrayed through holes to form the arrayed glass lenses by viscoelastic deformation. A higher forming temperature, pressure and longer time duration tend to produce the arrayed lenses with a higher peak height and a smaller radius of curvature. The arrayed chalcogenide glass lenses with a peak height of 430 μm can be obtained at a forming temperature of 305 °C, a gas pressure of 1 kg/cm2 and a time duration of 110 s. The contactless gas assisted molding system can avoid contact induced glass sticking and gas bubble problems. The surface qualities of molded lenses are much better than that of lenses molded by the traditional contact molding process.
關聯:	Journal of Non-Crystalline Solids 357(11–13), pp.2484–2488