    題名: Diamagnetic and Electrical Properties of SixMo2S3−x (x = 0.1, 0.2, 0.33, 0.5) and A0.1Mo2S3−x (A = C, B, and Ru)
    作者: Huang, G.T.;Chao, W.H.;Chang, J.K.;Liad, H.D.;Ling, D.C.;Chien, F.Z.;Wu, M. K.
    貢獻者: 淡江大學物理學系
    關鍵詞: SixMo2S3−x;Diamagnetic transition;Phase transition in resistivity
    日期: 2013-01
    上傳時間: 2013-04-07 00:27:11 (UTC+8)
    出版者: New York: Springer New York LLC
    摘要: Mo2S3 doped with Si, C, B, and Ru, is identified to bear the same crystalline structure P21/m as that of Mo2S3 through XRD analysis. Diamagnetic transitions with χm ∼ 10−4 emu/gOe at temperature ranging from 2 K to 6 K were observed in the doped samples of SixMo2S3−x (x = 0.1, 0.2, 0.33, 0.5). And both of the x = 0.2 and 0.5 samples were found to have double diamagnetic transitions with higher Tc at the same temperature of 6.01 K, while SixMo2S3−x of x = 0.33 displayed an extra ferromagneticlike response at 63 K. The corresponding transition in resistivity of SixMo2S3−x with x = 0.1 was noticed to show a mild drop with less than 10%of its original transition values as measured down to 2 K. But a superconducting-like magnetic field dependence on the phase transition of resistivity was also noted. Its diamagnetic signals were greatly reduced when the applied magnetic fields were raised to 103 Oes. In the doped samples of A0.1Mo2S2.9 (A = C, B, and Ru), the phase transition in resistivity at 4.08 K, 4.62 K, and 4.35 K, respectively, exhibited similar fashion as that in the case of Si0.1Mo2S2.9.
    關聯: Journal of Superconductivity and Novel Magnetism 26(3), pp.503–510
    DOI: 10.1007/s10948-013-2101-z
    顯示於類別:[物理學系暨研究所] 期刊論文


    檔案 描述 大小格式瀏覽次數
    Diamagnetic and Electrical Properties of SixMo2S3−x (x = 0.1, 0.2, 0.33, 0.5) and A0.1Mo2S3−x (A = C, B, and Ru).pdf1082KbAdobe PDF0檢視/開啟



    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - 回饋