淡江大學機構典藏:Item 987654321/82986
English  |  正體中文  |  简体中文  |  Items with full text/Total items : 62830/95882 (66%)
Visitors : 4039679      Online Users : 929
RC Version 7.0 © Powered By DSPACE, MIT. Enhanced by NTU Library & TKU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
    •  Adv. Search
    Home ‧ Login ‧ Upload ‧ Help ‧ About ‧ Administer Goto mobile version


    Please use this identifier to cite or link to this item: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/82986


    Title: Drawing and ultimate tenacity properties of polyamide 6/attapulgite composite fibers
    Authors: Tsai, Fang-Chang;Li, Peng;Liu, Zhi-Wei;Feng, Gang;Zhu, Ping;Wang, Chuen-Kai;Chen, Kan-Nan;Huang, Chi-Yuan;Yeh, Jen-taut
    Contributors: 淡江大學化學學系
    淡江大學化學工程暨材料工程學系
    Keywords: attapulgite;fiber;drawing;ultimate tenacity properties
    Date: 2012-12
    Issue Date: 2013-03-12 23:19:16 (UTC+8)
    Publisher: John Wiley & Sons, Inc.
    Abstract: The drawing and ultimate tenacity properties of the Polyamide 6 (PA6)/Attapulgite (ATP) composite fiber specimens prepared at varying modified ATP (mATP) contents and drawing condition were systematically investigated. As evidenced by Fourier transform infrared (FTIR) and morphological analysis, demarcated translucent resins were found firmly attached on the surfaces of ATP nanofibers. The specific surface areas of the mATP specimens reached a maximum value at 381 m2/g as the weight ratios of silane coupling agents to ATP nanofibers reached an optimum value at 1.0. The percentage crystallinity and melt shear viscosity values measured at varying shear rates of PA6x(mATP)y specimens increased consistently as their mATP contents increased. In contrast, melting temperatures of PA6x(mATP)y specimens reduced slightly as their mATP contents increased. At a fixed drawing temperature and rate, the achievable draw ratio (Dra) values of PA6x(mATP)y as-spun fiber specimens approach a maximum value, as their mATP contents are close to the 0.2 wt % optimum value. The maximum Dra values obtained for PA699.8(mATP)0.2 as-spun fiber specimens reached another maximum, when their drawing temperatures and rates approached the optimum values at 120°C and 50 mm/min, respectively. At a fixed draw ratio, the tenacity values of PA6x(mATP)y drawn fiber specimens drawn at the optimum drawing temperature and rate reached a maximum value, as their mATP contents approached the 0.2 wt % optimum value. Possible reasons accounting for the interesting morphological, specific surface area, drawing, orientation, and ultimate tenacity properties found for the PA6x(mATP)y fiber specimens are proposed.
    Relation: Journal of Applied Polymer Science 126(6), pp.1906-1916
    DOI: 10.1002/app.36970
    Appears in Collections:[Graduate Institute & Department of Chemistry] Journal Article

    Files in This Item:

    File Description SizeFormat
    68.pdfDrawing and ultimate tenacity properties of polyamide 6/attapulgite composite fibers679KbAdobe PDF300View/Open
    index.html0KbHTML326View/Open

    All items in 機構典藏 are protected by copyright, with all rights reserved.

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - Feedback