Preparation of water-resistant antifog hard coatings on plastic substrate

doi:10.1021/la304176k

淡江大學機構典藏 > 工學院 > 化學工程與材料工程學系暨研究所 > 期刊論文 > Item 987654321/80058

請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/80058

題名:	Preparation of water-resistant antifog hard coatings on plastic substrate
作者:	Chang, Chao-Ching;Huang, Feng-Hsi;Chang, Hsu-Hsien;Don, Trong-Ming;Chen, Ching-Chung;Cheng, Liao-Ping
貢獻者:	淡江大學化學工程與材料工程學系
日期:	2012-11-22
上傳時間:	2013-01-17 09:34:25 (UTC+8)
出版者:	American: American Chemical Society
摘要:	A novel water resistant antifog (AF) coating for plastic substrates was developed, which has a special hydrophilic/hydrophobic bilayer structure. The bottom layer, acting both as a mechanical support and a hydrophobic barrier against water penetration, is an organic–inorganic composite comprising colloidal silica embedded in a cross-linked network of dipentaethritol hexaacrylate (DPHA). Atop this layer, an AF coating is applied, which incorporates a superhydrophilic species synthesized from Tween-20 (surfactant), isophorone diisocyanate (coupling agent), and 2-hydroxyethyl methacrylate (monomer). Various methods, e.g., FTIR, SEM, AFM, contact angle, and steam test, were employed to characterize the prepared AF coatings. The results indicated that the size and the continuity of the hydrophilic domains on the top surface increased with increasing added amount of T20, however, at the expense of hardness, adhesiveness, and water resistivity. The optimal T20 content was found to be 10 wt %, at which capacity the resultant AF coating was transparent and wearable (5H, hardness) and could be soaked in water for 7 days at 25 °C without downgrading of its AF capability.
關聯:	Langmuir 28(49), pp.17193-17201
DOI:	10.1021/la304176k
顯示於類別:	[化學工程與材料工程學系暨研究所] 期刊論文

文件中的檔案:

檔案	大小	格式	瀏覽次數
index.html	0Kb	HTML	409	檢視/開啟
index.html	0Kb	HTML	308	檢視/開啟
Preparation of water-resistant antifog hard coatings on plastic substrate.pdf	1857Kb	Adobe PDF	1	檢視/開啟

在機構典藏中所有的資料項目都受到原著作權保護.

TAIR相關文章

資料載入中.....