    題名: Preparation and characterization of UV-sensitive chitosan for UV-cure with poly(ethylene glycol) dimethacrylate
    作者: Man-Chin Lin, Hung-Yin Tai, Ti-Cheng Ou, Don, Trong-Ming
    貢獻者: 淡江大學化學工程與材料工程學系
    日期: 2012-10
    上傳時間: 2013-01-17 09:30:36 (UTC+8)
    出版者: Springer Netherlands
    摘要: In this study, gel membranes of chitosan-g-poly(ethylene glycol) dimethacrylate (CS-g-PEGDMA) with pH sensitive properties were synthesized without employing any photo-initiator and crosslinker. First, CS was endowed with UV-sensitive property by reaction with cinnamoyl chloride in methanesulfonic acid. The reaction mainly occurred on the hydroxyl groups of the pyranose unit, while most C-2 amino groups were protected. The substitution degree of cinnamoyl group was 0.98, while the protection efficiency of –NH2 was about 80 %. Upon UV-irradiation, initial free radicals were produced only along the cinnamoyl-modified CS chains, which induced the grafting of PEGDMA from the chitosan chains and eventually the crosslinking. Increasing the feeding amount of PEGDMA increased the grafting ratio as well as the crosslinking density. The Tg value decreased from 161 °C for the pure chitosan to about 90 °C for the CS-g-PEGDMA with a grafting ratio of 1.29. Two stages of degradation correspondent to the individual degradation of CS chains and the PEGDMA chains were observed for all CS-g-PEGDMA copolymers, demonstrating their nature of graft copolymers. The tensile mechanical properties of the CS-g-PEGDMA membranes were affected by the two opposing factors: inter-connected soft PEGDMA chains and crosslinking density; and the optimum properties were achieved when the grafting ratio was increased to about 0.80. By combining CS and PEGDMA components, these copolymer membranes thus have the potential to be used as biomedical membranes.
    關聯: Cellulose 19(5), pp.1689–1700
    DOI: DOI 10.1007/s10570-012-9758-5
    顯示於類別:[化學工程與材料工程學系暨研究所] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    CS CIN PEGMA UV Cellulose 2012.pdf1011KbAdobe PDF1018檢視/開啟
    index.html0KbHTML115檢視/開啟

    在機構典藏中所有的資料項目都受到原著作權保護.

    TAIR相關文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - 回饋