Direct observation and mechanism of increased emission sites in Fe-coated microcrystalline diamond films

doi:10.1063/1.4729836

淡江大學機構典藏 > 理學院 > 物理學系暨研究所 > 期刊論文 > Item 987654321/78971

請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/78971

題名:	Direct observation and mechanism of increased emission sites in Fe-coated microcrystalline diamond films
作者:	Panda, Kalpataru;Sundaravel, B.;Panigrahi, B. K.;Huang, Pin-chang;Shih, Wen-ching;Chen, Huang-chin;Lin, I-nan
貢獻者:	淡江大學物理學系
日期:	2012-06
上傳時間:	2012-11-07 15:05:50 (UTC+8)
出版者:	American Institute of Physics(AIP)
摘要:	The electron field emission (EFE) properties of microcrystalline diamond(MCD) films are significantly enhanced due to the Fe coating and post-annealing processes. The 900 °C post-annealed Fe coated diamond films exhibit the best EFE properties, with a turn on field (E0) of 3.42 V/μm and attain EFE current density (Je) of 170 μA/cm2 at 7.5 V/μm. Scanning tunnelling spectroscopy (STS) in current imaging tunnelling spectroscopy mode clearly shows the increased number density of emission sites in Fe-coated and post-annealed MCD films than the as-prepared ones. Emission is seen from the boundaries of the Fe (or Fe3C) nanoparticles formed during the annealing process. In STS measurement, the normalized conductance dI/dVI/V versus V curves indicate nearly metallic band gap, at the boundaries of Fe (or Fe3C) nanoparticles. Microstructural analysis indicates that the mechanism for improved EFE properties is due to the formation of nanographite that surrounds the Fe (or Fe3C) nanoparticles.
關聯:	Journal of Applied Physics 111(12), pp.124309 (9 pages)
DOI:	10.1063/1.4729836
顯示於類別:	[物理學系暨研究所] 期刊論文

文件中的檔案:

檔案	描述	大小	格式	瀏覽次數
1.4729836.pdf		3311Kb	Adobe PDF	455	檢視/開啟
index.html		0Kb	HTML	297	檢視/開啟

在機構典藏中所有的資料項目都受到原著作權保護.

TAIR相關文章

資料載入中.....