Bias-enhanced nucleation and growth processes for improving the electron field emission properties of diamond films

doi:10.1063/1.3687918

淡江大學機構典藏 > 理學院 > 物理學系暨研究所 > 期刊論文 > Item 987654321/78969

請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/78969

題名:	Bias-enhanced nucleation and growth processes for improving the electron field emission properties of diamond films
作者:	Teng, Kuang-yau;Chen, Huang-chin;Tzeng, Gaung-chin;Tang, Chen-yau;Cheng, Hsiu-fung;Lin, I-nan
貢獻者:	淡江大學物理學系
日期:	2012-03
上傳時間:	2012-11-07 15:00:58 (UTC+8)
出版者:	College Park: American Institute of Physics(AIP)
摘要:	The evolution of diamond films in bias-enhanced-nucleation (BEN) and bias-enhanced-growth (BEG) processes was systematically investigated. While the BEN process can efficiently form diamond nuclei on the Si substrates, BEG with large enough applied field (> –400 V) and for sufficiently long periods (>60 min) was needed to develop proper granular structure for the diamond films so as to enhance the electron field emission (EFE) properties of the films. For the films BEG under -400 V for 60 min (after BEN for 10 min), the EFE process can be turned on at a field as small as 3.6 V/μm, attaining a EFE current density as large as 325 μA/cm2 at an applied field of 15 V/μm. Such an EFE behavior is even better than that of the ultrananocrystalline diamond films grown in CH4/Ar plasma. Transmission electron microscopic examination reveals that the prime factor enhancing the EFE properties of these films is the induction of the nano-graphite filaments along the thickness of the films that facilitates the transport of electrons through the films.
關聯:	Journal of Applied Physics 111(5), 053701(10pages)
DOI:	10.1063/1.3687918
顯示於類別:	[物理學系暨研究所] 期刊論文

文件中的檔案:

檔案	大小	格式	瀏覽次數
1.3687918.pdf	4508Kb	Adobe PDF	629	檢視/開啟
index.html	0Kb	HTML	266	檢視/開啟
index.html	0Kb	HTML	161	檢視/開啟

在機構典藏中所有的資料項目都受到原著作權保護.

TAIR相關文章

資料載入中.....