    題名: Field emission enhancement in ultrananocrystalline diamond films by in situ heating during single or multienergy ion implantation processes
    作者: Joseph, P.T.;Tai, N.H.;Chen, C.H.;Niu, H.;Cheng, H.F.;Palnitkar, U.A.;Lin, I.N.
    貢獻者: 淡江大學物理學系
    日期: 2009-06
    上傳時間: 2012-06-14 09:23:53 (UTC+8)
    出版者: College Park: American Institute of Physics
    摘要: The single or multienergy nitrogen (N) ion implantation (MENII) processes with a dose (4×1014 ions/cm2) just below the critical dose (1×1015 ions/cm2) for the structural transformation of ultrananocrystalline diamond (UNCD) films were observed to significantly improve the electron field emission (EFE) properties. The single energy N ion implantation at 300 °C has shown better field emission properties with turn-on field (E0) of 7.1 V/μm, as compared to room temperature implanted sample at similar conditions (E0 = 8.0 V/μm) or the pristine UNCD film (E0 = 13.9 V/μm). On the other hand, the MENII with a specific sequence of implantation pronouncedly showed different effect on altering the EFE properties for UNCD films, and the implantation at 300 °C further enhanced the EFE behavior. The best EFE characteristics achieved for the UNCD film treated with the implantation process are E0 = 4.5 V/μm and current density of (Je) = 2.0 mA/cm2 (at 24.5 V/μm). The prime factors for improving the EFE properties are presumed to be the grain boundary incorporation and activation of the implanted N and the healing of induced defects, which are explained based on surface charge transfer doping mechanism.
    關聯: Journal of Applied Physics 105(12), 123710(7pages)
    DOI: 10.1063/1.3152790
    顯示於類別:[物理學系暨研究所] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    1089-7550_105(12)p123710.pdf837KbAdobe PDF449檢視/開啟
    index.html0KbHTML36檢視/開啟

    在機構典藏中所有的資料項目都受到原著作權保護.

    TAIR相關文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - 回饋