    題名: Ultradrawing properties of ultrahigh- molecular-weight polyethylene/carbon nanotube fibers prepared at various formation temperatures
    作者: Yeh, Jen-taut;Lai, Yu-ching;Hai, Liu;Shu, Yao-chi;Huang Chi-yuan;Huang Kuo-shien;Chen Kan-nan
    貢獻者: 淡江大學化學學系
    關鍵詞: ultrahigh-molecular-weight polyethylene;carbon nanotubes;formation temperatures
    日期: 2011-01
    上傳時間: 2012-06-14 09:09:01 (UTC+8)
    出版者: Chichester: John Wiley & Sons Ltd.
    摘要: The influence of formation temperature on the ultradrawing properties of ultrahigh-molecular-weight polyethylene/carbon nanotube (UHMWPE/CNT) fiber specimens is investigated. Gel solutions of UHMWPE/CNT with various CNT contents were gel-spun at the optimum concentration and temperature but were cooled at varying formation temperatures in order to improve the ultradrawing and tensile properties of the UHMWPE/CNT composite fibers. The achievable draw ratio (Dra) values of UHMWPE/CNT as-prepared fibers reach a maximum when they are prepared with the optimum CNT content and formation temperature. The Dra value of UHMWPE/CNT as-prepared fibers produced using the optimum CNT content and formation temperature is about 33% higher than that of UHMWPE as-prepared fibers produced using the optimum concentration and formation temperature. The percentage crystallinity (Wc) and melting temperature (Tm) of UHMWPE/CNT as-prepared fiber specimens increase significantly as the formation temperature increases. In contrast, Wc increases but Tm decreases significantly as the CNT content increases. Dynamic mechanical analysis of UHMWPE and UHMWPE/CNT fiber specimens exhibits particularly high α-transition and low β-transition, wherein the peak temperatures of α-transition and β-transition increase dramatically as the formation temperature increases and/or CNT content decreases. In order to understand these interesting drawing, thermal and dynamic mechanical properties of the UHMWPE and UHMWPE/CNT as-prepared fiber specimens, birefringence, morphological and tensile studies of as-prepared and drawn fibers were carried out. Possible mechanisms accounting for these interesting properties are proposed.
    關聯: Polymer international 60(1), pp.59-68
    DOI: 10.1002/pi.2911
    顯示於類別:[化學學系暨研究所] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    0959-8103_60(1)p59-68.pdf205KbAdobe PDF299檢視/開啟
    Ultradrawing properties of ultrahigh- molecular-weight polyethylenecarbon nanotube fibers prepared at various formation temperatures.pdf412KbAdobe PDF1檢視/開啟

    在機構典藏中所有的資料項目都受到原著作權保護.

    TAIR相關文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - 回饋