Effects of Surface Modification by Argon Plasma on Peel Strength of Woven-type Ultrahigh- Molecular-Weight Polyethylene

doi:10.1143/JJAP.49.08JA01

淡江大學機構典藏 > 理學院 > 化學學系暨研究所 > 期刊論文 > Item 987654321/77228

請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/77228

題名:	Effects of Surface Modification by Argon Plasma on Peel Strength of Woven-type Ultrahigh- Molecular-Weight Polyethylene
作者:	Wu, Jing-yi;Lin, Sheng-kai;Tsai, Ching-shan;Huang, Chi-yuan;Yeh, Jen-taut;Chen, Ken-nan
貢獻者:	淡江大學化學學系
日期:	2010-08
上傳時間:	2012-06-14 09:07:08 (UTC+8)
出版者:	Tokyo: Institute of Pure and Applied Physics
摘要:	In this investigation, the effects of surface modification by argon plasma on peel strength of woven-type ultrahigh-molecular-weight polyethylene (WUHMWPE) fibers were studied. After plasma treatment, free radicals were generated on the WUHMWPE surface and then converted to peroxide by exposure to air. The optimum free radical content for realizing high T-peel strength was 1.27× 10-9 mol/mm2 for plasma treatment at 40 W for 4 min. The plasma-treated WUHMWPE (PWUHMWPE) fiber exhibited the hydrophilic property and many anchors. Regarding bonding, the chemical bonding force significantly increased with adhesion strength between the PWUHMWPE fiber and adhesive 3M 1099. Scanning electron microscopy (SEM) images showed that the surface of the PWUHMWPE fibers contained many fibrils. These fibrils can provide peel strength during T-peel testing. Regarding surface modification by plasma treatment, the peel strength of the WUHMWPE surface with adhesive 3M 1099 was increased from 2.58 to 4.39 kgf/in.
關聯:	Japanese Journal of Applied Physics 49(8), 08JA01(5pages)
DOI:	10.1143/JJAP.49.08JA01
顯示於類別:	[化學學系暨研究所] 期刊論文

文件中的檔案:

檔案	描述	大小	格式	瀏覽次數
1347-4065_49(8)p08JA01.pdf		504Kb	Adobe PDF	220	檢視/開啟
Effects of Surface Modification by Argon Plasma on Peel Strength of Woven-type Ultrahigh- Molecular-Weight Polyethylene.pdf		583Kb	Adobe PDF	5	檢視/開啟

在機構典藏中所有的資料項目都受到原著作權保護.

TAIR相關文章

資料載入中.....