    题名: Effects of Surface Modification by Argon Plasma on Peel Strength of Woven-type Ultrahigh- Molecular-Weight Polyethylene
    作者: Wu, Jing-yi;Lin, Sheng-kai;Tsai, Ching-shan;Huang, Chi-yuan;Yeh, Jen-taut;Chen, Ken-nan
    贡献者: 淡江大學化學學系
    日期: 2010-08
    上传时间: 2012-06-14 09:07:08 (UTC+8)
    出版者: Tokyo: Institute of Pure and Applied Physics
    摘要: In this investigation, the effects of surface modification by argon plasma on peel strength of woven-type ultrahigh-molecular-weight polyethylene (WUHMWPE) fibers were studied. After plasma treatment, free radicals were generated on the WUHMWPE surface and then converted to peroxide by exposure to air. The optimum free radical content for realizing high T-peel strength was 1.27× 10-9 mol/mm2 for plasma treatment at 40 W for 4 min. The plasma-treated WUHMWPE (PWUHMWPE) fiber exhibited the hydrophilic property and many anchors. Regarding bonding, the chemical bonding force significantly increased with adhesion strength between the PWUHMWPE fiber and adhesive 3M 1099. Scanning electron microscopy (SEM) images showed that the surface of the PWUHMWPE fibers contained many fibrils. These fibrils can provide peel strength during T-peel testing. Regarding surface modification by plasma treatment, the peel strength of the WUHMWPE surface with adhesive 3M 1099 was increased from 2.58 to 4.39 kgf/in.
    關聯: Japanese Journal of Applied Physics 49(8), 08JA01(5pages)
    DOI: 10.1143/JJAP.49.08JA01
    显示于类别:[化學學系暨研究所] 期刊論文

    文件中的档案:

    档案 描述 大小格式浏览次数
    1347-4065_49(8)p08JA01.pdf504KbAdobe PDF201检视/开启
    Effects of Surface Modification by Argon Plasma on Peel Strength of Woven-type Ultrahigh- Molecular-Weight Polyethylene.pdf583KbAdobe PDF5检视/开启