Preparation of microporous poly(VDF-co-HFP) membranes by template-leaching method

doi:10.1016/j.seppur.2010.02.001

淡江大學機構典藏 > 工學院 > 化學工程與材料工程學系暨研究所 > 期刊論文 > Item 987654321/77224

請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/77224

題名:	Preparation of microporous poly(VDF-co-HFP) membranes by template-leaching method
作者:	Chang, Hsu-Hsien;Yao, Liang-Chin;Lin, Dar-Jong;Cheng, Liao-Ping
貢獻者:	淡江大學化學工程與材料工程學系
關鍵詞:	Poly(vinylidene fluoride);Porous membrane;Copolymer;Polymer blend
日期:	2010-04
上傳時間:	2012-06-14 09:03:33 (UTC+8)
出版者:	Kidlington: Pergamon
摘要:	The copolymer of vinylidene fluoride and hexafluoro propylene, poly(VDF–HFP), and the terpolymer of vinylidene fluoride, tetrafluoro ethylene, and hexafluoro propylene, poly(VDF–TEF–HFP), were solution blended at first to form dense composite films. Then, 90% acetone aqueous solution was used to leach out the terpolymer in the film at 5 °C. By varying the fraction of terpolymer in the blend and the leaching condition, microporousmembranes with different porous morphology were produced, as revealed by SEM imaging. When the terpolymer content in the blend was lower than 30 wt%, low porosity (e.g., 24%) asymmetric membranes were obtained. On the other hand, when the terpolymer content approached 50%, skinless membranes with uniform pore distribution (pore size, ca. 1 μm) were produced. These skinless membranes demonstrate high tensile strengths (∼6 MPa) and water fluxes (3000–8000 LMH) that are potentially applicable to micro-filtration operations. Furthermore, crystallinities of the membranes were determined both by X-ray diffractometry and differential scanning calorimetry. Both methods indicated crystallinity near 24%, typical of poly(VDF–HFP) polymer in different forms.
關聯:	Separation and Purification Technology 72(2), pp. 156-166
DOI:	10.1016/j.seppur.2010.02.001
顯示於類別:	[化學工程與材料工程學系暨研究所] 期刊論文

文件中的檔案:

檔案	描述	大小	格式	瀏覽次數
1383-5866_72(2)p156-166.pdf		3194Kb	Adobe PDF	292	檢視/開啟

在機構典藏中所有的資料項目都受到原著作權保護.

TAIR相關文章

資料載入中.....