Preparation of microporous poly(VDF-co-HFP) membranes by template-leaching method

doi:10.1016/j.seppur.2010.02.001

淡江大學機構典藏 > 工學院 > 化學工程與材料工程學系暨研究所 > 期刊論文 > Item 987654321/77224

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/77224

题名:	Preparation of microporous poly(VDF-co-HFP) membranes by template-leaching method
作者:	Chang, Hsu-Hsien;Yao, Liang-Chin;Lin, Dar-Jong;Cheng, Liao-Ping
贡献者:	淡江大學化學工程與材料工程學系
关键词:	Poly(vinylidene fluoride);Porous membrane;Copolymer;Polymer blend
日期:	2010-04
上传时间:	2012-06-14 09:03:33 (UTC+8)
出版者:	Kidlington: Pergamon
摘要:	The copolymer of vinylidene fluoride and hexafluoro propylene, poly(VDF–HFP), and the terpolymer of vinylidene fluoride, tetrafluoro ethylene, and hexafluoro propylene, poly(VDF–TEF–HFP), were solution blended at first to form dense composite films. Then, 90% acetone aqueous solution was used to leach out the terpolymer in the film at 5 °C. By varying the fraction of terpolymer in the blend and the leaching condition, microporousmembranes with different porous morphology were produced, as revealed by SEM imaging. When the terpolymer content in the blend was lower than 30 wt%, low porosity (e.g., 24%) asymmetric membranes were obtained. On the other hand, when the terpolymer content approached 50%, skinless membranes with uniform pore distribution (pore size, ca. 1 μm) were produced. These skinless membranes demonstrate high tensile strengths (∼6 MPa) and water fluxes (3000–8000 LMH) that are potentially applicable to micro-filtration operations. Furthermore, crystallinities of the membranes were determined both by X-ray diffractometry and differential scanning calorimetry. Both methods indicated crystallinity near 24%, typical of poly(VDF–HFP) polymer in different forms.
關聯:	Separation and Purification Technology 72(2), pp. 156-166
DOI:	10.1016/j.seppur.2010.02.001
显示于类别:	[化學工程與材料工程學系暨研究所] 期刊論文

文件中的档案:

档案	描述	大小	格式	浏览次数
1383-5866_72(2)p156-166.pdf		3194Kb	Adobe PDF	288	检视/开启

在機構典藏中所有的数据项都受到原著作权保护.

TAIR相关文章

数据加载中.....