Conductive composite particles synthesized via pickering emulsion polymerization using conductive latex of poly(3,4-ethylenedioxythiophene) (PEDOT) as stabilizer

doi:10.1016/j.polymer.2012.01.005

淡江大學機構典藏 > 工學院 > 化學工程與材料工程學系暨研究所 > 期刊論文 > Item 987654321/75127

請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/75127

題名:	Conductive composite particles synthesized via pickering emulsion polymerization using conductive latex of poly(3,4-ethylenedioxythiophene) (PEDOT) as stabilizer
作者:	Wu, Chieh-Han;Chiu, Wen-Yen;Don, Trong-Ming
貢獻者:	淡江大學化學工程與材料工程學系
關鍵詞:	Pickering emulsion polymerization;PEDOT;Conductive film
日期:	2012-02
上傳時間:	2012-03-13 10:42:48 (UTC+8)
出版者:	London: Elsevier Ltd
摘要:	In this research, poly(3,4-ethylenedioxythiophene) (PEDOT) nanoparticles less than 100 nm were synthesized first and applied as the solid stabilizer for producing PEDOT-polystyrene (PEDOT-PSt) composite latex by Pickering emulsion polymerization. The results showed that most PEDOT nanoparticles adhered to the PSt core particles having the size from 100 to 250 nm. By casting the latex, the obtained PEDOT-PSt film had a surface resistance of 4–5 kΩ/□, almost the same as the pure PEDOT film, though its PEDOT content was only 6.2 wt%. Those PEDOT nanoparticles in the outer layer could contact with one another, forming a continuous network as the conductive passageway. Furthermore, soft latex particles of poly(styrene-co-butyl acrylate), P(St-BA), were synthesized and mixed with the conducting rigid PEDOT-PSt latex for improving the toughness and transparency of the casting film. A critical point at about 2 wt% of PEDOT content in the PEDOT-PSt/P(St-BA) film was observed in the surface resistance measurement.
關聯:	Polymer 53(5), pp.1086–1092
DOI:	10.1016/j.polymer.2012.01.005
顯示於類別:	[化學工程與材料工程學系暨研究所] 期刊論文

文件中的檔案:

檔案	描述	大小	格式	瀏覽次數
PEDOT polymer 2012.pdf		1249Kb	Adobe PDF	387	檢視/開啟

在機構典藏中所有的資料項目都受到原著作權保護.

TAIR相關文章

資料載入中.....