    題名: Effect of initiator on the over-voltage positive temperature coefficient of linear low density polyethylene/carbon black nano composites
    作者: 陳幹男
    貢獻者: 淡江大學化學學系
    日期: 2010-05-01
    上傳時間: 2011-10-15 23:17:51 (UTC+8)
    摘要: The composite of linear low density polyethylene (LLDPE) with carbon black (CB) and inorganic flame retardant (aluminum hydroxide, Al(OH)3) was prepared by melt-blending method. The effect of cross-linking on the stability of positive temperature coefficient (PTC) of composite and the elimination of negative temperature coefficient (NTC) of composite were investigated. LLDPE was chemically cross-linking with different contents of initiator (dicumyl peroxide, DCP). The cross-linking effects of composite were analyzed by gel content analysis, differential scanning calorimetry (DSC), and dynamic mechanical analysis (DMA). By the effect of DCP, not only the composite appeared a high PTC intensity, but also the NTC effect of composite was eliminated. In this investigation, the optimum PTC intensity of composite reached 5.87 orders of magnitude for the composition of LLD0.l0C33.7A28, and the PTC transitional temperature of composite decreased with increasing of DCP content. In addition, the good reproducibility of composites was proved by thermal cycling, and successfully passed the test of over-voltage resistance.
    關聯: Macromol. Symposia.286, pp.125-134
    DOI: 10.1002/masy.200951216
    顯示於類別:[化學工程與材料工程學系暨研究所] 期刊論文

    文件中的檔案:

    沒有與此文件相關的檔案.

    在機構典藏中所有的資料項目都受到原著作權保護.

    TAIR相關文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - 回饋