Preparation of magnetic cobalt-based catalyst for hydrogen generation from alkaline NaBH4 solution

doi:10.1016/j.apcatb.2009.06.003

淡江大學機構典藏 > 工學院 > 化學工程與材料工程學系暨研究所 > 期刊論文 > Item 987654321/60398

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/60398

题名:	Preparation of magnetic cobalt-based catalyst for hydrogen generation from alkaline NaBH4 solution
作者:	Liu, Cheng-Hong;Chen, Bing-Hung;Hsueh, Chan-Li;Ku, Jie-Ren;Tsau, Fanghei;Hwang, Kuo-Jen
贡献者:	淡江大學化學工程與材料工程學系
关键词:	Hydrogen generation;Cobalt-based catalyst;Sodium borohydride;Wet-chemical reduction process;Fuel cell
日期:	2009-09
上传时间:	2011-10-13 22:37:34 (UTC+8)
出版者:	Amsterdam: Elsevier BV
摘要:	A fast and simple fabrication process, viz. a wet-chemical reduction process, was utilized for preparation of a cobalt-based catalyst to be used for hydrogen generation from alkaline NaBH4 solution. Characteristics of this cobalt-based catalyst were carried out by using various instruments, such as SEM/EDS, XPS, ICP, VSM, BET and TGA. The surface chemistry of the obtained catalyst is mainly cobalt oxides, not cobalt borides. Ferromagnetic property of the cobalt-based catalyst makes it convenient for being recycled from spent NaBH4 solution. The rate of hydrogen generation from catalyzed hydrolysis of alkaline NaBH4 solution was determined as a function of temperature, NaBH4 concentration, and NaOH concentration in the presence of prepared catalysts. In general, stable generation rate of highly pure hydrogen near 200 mL min−1 g−1 was achieved in 100 mL of 5 wt% NaBH4 solution containing 5 wt% NaOH solution and 200 mg of Co/IR-120 catalyst, in which no temperature runoff was observed during the course of hydrogen production. The activation energy of NaBH4 hydrolysis reaction was found at 66.67 kJ mol−1, which was comparable with others reported in the open literatures.
關聯:	Applied Catalysis B-Environmental 91(1-2), pp.368-379
DOI:	10.1016/j.apcatb.2009.06.003
显示于类别:	[化學工程與材料工程學系暨研究所] 期刊論文

文件中的档案:

档案	大小	格式	浏览次数
index.html	0Kb	HTML	260	检视/开启

在機構典藏中所有的数据项都受到原著作权保护.

TAIR相关文章

数据加载中.....