    题名: Enhancing thermal stability and photocatalytic activity of anatase-TiO2 nanoparticles by co-doping P and Si elements.pdf
    作者: Yu, Hsuan-Fu;Yang, Shih-Te
    贡献者: 淡江大學化學工程與材料工程學系
    关键词: Titanium dioxide;Sol–gel process;Nanoparticles;Photocatalysis;Structural transformation
    日期: 2010-03
    上传时间: 2011-10-13 22:31:41 (UTC+8)
    出版者: Amsterdam: Elsevier BV
    摘要: The Si/P–TiO2 nanoparticles, with a molar ratio [Si + P]/[Si/P–TiO2] = 0.03, were synthesized using a sol–gel method. The effects of relative ratios of dopants (i.e., R ≡ [P]/([Si + P]) and calcination temperatures on phase transformation, grain growth, and photocatalytic activity of the gel-derived Si/P–TiO2 were examined. While the Si–TiO2 (i.e., R = 0) had its anatase structure stabilize at 700 °C for 2 h, the Si/P–TiO2 (i.e., 0.33 ≤ R < 1) and P–TiO2 (i.e., R = 1) were able to preserve the anatase-TiO2 at temperature as high as 900 °C. Although at 900 °C the phosphorus elements in Si/P–TiO2 nanoparticles were partly excluded to the particles’ surface and tended to fuse the adjacent particles together, which may lead to a large reduction in their specific surface areas and photocatalytic activities, the Si/P–TiO2 with high silicon contents, such as the particles of R = 0.5 and 0.33, were still composed of loosely packed nanoparticles and showed good photocatalytic ability. In whole, the Si/P–TiO2 nanoparticles of R = 0.5 calcined at 600–900 °C gave the superior performance in photocatalytic activity, under both 365-nm UV light and white light irradiation.
    關聯: Journal of Alloys and Compounds 492(1-2), pp.695-700
    DOI: 10.1016/j.jallcom.2009.12.021
    显示于类别:[化學工程與材料工程學系暨研究所] 期刊論文

    文件中的档案:

    档案 大小格式浏览次数
    index.html0KbHTML209检视/开启

    在機構典藏中所有的数据项都受到原著作权保护.

    TAIR相关文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - 回馈