Effects of heating atmosphere on formation of crystalline citrate-derived LaAlO3 nanoparticles

doi:10.1016/j.jallcom.2010.10.109

淡江大學機構典藏 > 工學院 > 化學工程與材料工程學系暨研究所 > 期刊論文 > Item 987654321/60362

請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/60362

題名:	Effects of heating atmosphere on formation of crystalline citrate-derived LaAlO3 nanoparticles
作者:	Yu, Hsuan-Fu;Guo, Yu-Man
貢獻者:	淡江大學化學工程與材料工程學系
關鍵詞:	Lanthanum aluminate;Citrate precursor method;Thermal analysis;Calcination atmosphere;Ceramic synthesis
日期:	2011-02
上傳時間:	2011-10-13 22:31:11 (UTC+8)
出版者:	Amsterdam: Elsevier BV
摘要:	Crystalline LaAlO3 nanoparticles were synthesized at relative low temperatures, using a citrate-precursor technique. La(NO3)3, Al(NO3)3, and C3H4(OH)(COOH)3, in a molar ratio of 1:1:1, were dissolved in deionized water. NH4OH was used to adjust the aqueous solution to pH 7. After drying, the citrate precursors were charred at 350 °C, followed by calcination at different temperatures, in air or oxygen atmosphere. The thermochemical properties of the resultant particles were analyzed using thermogravimetric and differential thermal analysis, X-ray diffractometry, infrared spectroscopy, scanning electron microscopy, and transmission electron microscopy. Effects of calcination temperature and heating atmosphere on the formation of crystalline LaAlO3 nanoparticles were investigated. In O2 atmosphere, clacining the citrate-derived charred solid precursor at 700 °C for 3 h can decompose all intermediates to produce pure LaAlO3 nanoparticles (particle sizes ≤ 100 nm) with an average crystallite size of about 24 nm and possessing high sinterability.
關聯:	Journal of Alloys and Compounds 509(5), pp.1984-1988
DOI:	10.1016/j.jallcom.2010.10.109
顯示於類別:	[化學工程與材料工程學系暨研究所] 期刊論文

文件中的檔案:

檔案	描述	大小	格式	瀏覽次數
0925-8388_509(5)p1984-1988.pdf		999Kb	Adobe PDF	203	檢視/開啟
0925-8388_509(5)p1984-1988.pdf		999Kb	Adobe PDF	1	檢視/開啟

在機構典藏中所有的資料項目都受到原著作權保護.

TAIR相關文章

資料載入中.....