    題名: Monolithic n-type conductivity on low temperature grown freestanding ultrananocrystalline diamond films
    作者: Joseph, P. T.;Tai, N. H.;Lin, I-Nan
    貢獻者: 淡江大學物理學系
    日期: 2010-06
    上傳時間: 2011-09-30 22:01:39 (UTC+8)
    出版者: College Park: American Institute of Physics
    摘要: We report monolithic n-type conductivity on low-temperature (<570 °C) grown ultrananocrystalline diamond (UNCD) films by Li-diffusion (about 255 nm) from LiNbO3 substrates. Low resistivity of 1.2 Ω cm with carrier concentration of −2×1020 cm−3 is obtained on freestanding UNCD films. The films bonded to Cu-tape show very low turn-on field of 4.2 V/μm with emission current density of above 0.3 mA/cm2 at a low applied filed of 10 V/μm. The n-type conductivity of low-temperature Li-diffused UNCD films overwhelms that of the high-temperature (≥800 °C) nitrogen doped ones and will make a significant impact to diamond-based electronics.
    關聯: Applied Physics Letters 97(4), 042107(3pages)
    DOI: 10.1063/1.3472204
    顯示於類別:[物理學系暨研究所] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    0003-6951_97(4)_p042107.pdf580KbAdobe PDF407檢視/開啟

    在機構典藏中所有的資料項目都受到原著作權保護.

    TAIR相關文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - 回饋