Electron field emission properties of carbon nanoflakes prepared by RF sputtering

淡江大學機構典藏 > 理學院 > 物理學系暨研究所 > 期刊論文 > Item 987654321/58293

請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/58293

題名:	Electron field emission properties of carbon nanoflakes prepared by RF sputtering
作者:	林諭男;Shih, Wen-ching;Jeng, Jian-min;Lo, Jyi-tsong
貢獻者:	淡江大學物理學系
日期:	2010-11-01
上傳時間:	2011-09-30 22:00:09 (UTC+8)
摘要:	Carbon nanoflakes (CNFs) with corrugated geometry were synthesized using RF sputtering process with Ar/CH4 gas mixture. Transmission electron microscopic examination reveals that the introduction of H2 in sputtering chamber leads to the preferential etching of amorphous carbons, while maintaining integrity for the nano-crystalline phases. The proportion of nano-sized crystalline clusters is thus increased, which improved the electron field emission (EFE) properties of the materials, viz. with turn-on field of E0 = 6.22 V/μm and FEE current density of Je = 90.1 μA/cm2 at 11.0 V/μm. The cathodes made of screen printing of CNFs-Ag paste exhibit even better EFE properties than the as-deposited CNFs. The EFE of the CNFs cathodes can be turned on at E0 = 5.71 V/μm, achieving J0 = 340.1 μA/cm2 at 11.0 V/μm applied field. These results showed that the CNFs are inheritantly more robust in device fabrication process than the other carbon materials and thus possess better potential for electron field emitter applications.
關聯:	J Mater Sci: Mater Electron21, pp.926-931
DOI:	10.1007/s10854-009-0019-9
顯示於類別:	[物理學系暨研究所] 期刊論文

文件中的檔案:

檔案	描述	大小	格式	瀏覽次數
Electron field emission properties of carbon nanoflakes prepared by RF sputtering.pdf		556Kb	Adobe PDF	2	檢視/開啟
index.html		0Kb	HTML	46	檢視/開啟

在機構典藏中所有的資料項目都受到原著作權保護.

TAIR相關文章