淡江大學機構典藏:Item 987654321/5545
English  |  正體中文  |  简体中文  |  Items with full text/Total items : 62805/95882 (66%)
Visitors : 3924877      Online Users : 711
RC Version 7.0 © Powered By DSPACE, MIT. Enhanced by NTU Library & TKU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
    •  Adv. Search
    Home ‧ Login ‧ Upload ‧ Help ‧ About ‧ Administer Goto mobile version


    Please use this identifier to cite or link to this item: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/5545


    Title: 合成增容劑對聚乙烯與聚醯胺奈米混成材料之探討
    Other Titles: Nano-Composites of Polyethylene and Polyamide via the Preparative Compatibilizer
    Authors: 陳幹男
    Contributors: 淡江大學化學學系
    Date: 2002
    Issue Date: 2010-04-19 11:33:24 (UTC+8)
    Abstract: 本計畫以熔融法研究高密度聚乙烯(HDPE)與耐隆-6(PA6)之相容行為。將馬來酐(MAH)及苯乙烯或MANA4(鈉離子化之馬來酸) 或SMA (苯乙烯和馬來酐之共聚物 ) 與起始劑DCP (過氧化異丙苯) 利用自由基反應以熔融法接枝於高密度聚乙烯上；再將耐隆-6 加入此熔融系統中使於高密度聚乙烯與耐隆-6 之界面上原位生成(in--situ formation)其所需之相容性共聚物，而此相容性共聚物即於此摻合系統中充當相容劑，以減少高密度聚乙烯與耐隆-6 之界面張力及增加其界面黏著力，有效地提高了高密度聚乙烯與耐隆-6之相容性。以FT-IR 光譜上可以觀測到接枝反應及相容化前後之不同，並可以定量其接枝率之多寡。以SEM( 掃描式電子顯微鏡 )明顯地看到加了反應性單體之高密度聚乙烯與耐隆-6 摻合系統的分散相減小及界面黏著力提升，足以顯示系統相容性之提高。依DSC ( 微差掃描式熱分析 ) 、 TGA ( 熱重分析 ) 、 XRD ( X光繞射分析 )等測試分析之結果亦證明了此一系列原位相容反應能提升高密度聚乙烯與耐隆-6 摻合系統之相容性。
    Compatibilizers were prepared for the blends of high-density polyethylene (HDPE) and polyamide-6 (Nylon 6). A compatibilizer precursor (CP) was prepared from a grafting reaction of maleic anhydride/styrene, partial neutralized maleic acid or styrene/maleic anhydride copolymer on molten HDPE, respectively by a free radical process and dicummyl peroxide was an initiator. Then polyamide (Nylon-6) was added in the subsequent process and formed in situ compatabilizer for HDPE/Nylon-6 blend. The better compatibility was resulted and demonstrated on decreasing surface tension and increasing adhesion between HDPE and Nylon-6. The grafting percentage of HDPE was measured byFT-IR. The compatibility and the adhesion between HDPE and Nylon-6 were improved and exhibited on SEM and XRD.The thermal properties on TGA and DSC also demonstrated the better compatibility resulted from the in-situ compatibilizer formation occurred during the process.
    Appears in Collections:[Graduate Institute & Department of Chemistry] Research Paper

    Files in This Item:

    File Description SizeFormat
    912216E032001.pdf238KbAdobe PDF723View/Open

    All items in 機構典藏 are protected by copyright, with all rights reserved.

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - Feedback