The Effect of Heat Treatment on Interface Properties of S45C Steel/Copper Compound Casting

淡江大學機構典藏 > 工學院 > 機械與機電工程學系暨研究所 > 期刊論文 > Item 987654321/52788

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/52788

题名:	The Effect of Heat Treatment on Interface Properties of S45C Steel/Copper Compound Casting
作者:	何金新;Ho, Jin-shin;林清彬;Lin, C. B.
贡献者:	淡江大學機械與機電工程學系
关键词:	S45C;Copper;Cast welding;Marquenching;Martempering;Austempering
日期:	2003-03-01
上传时间:	2010-12-01 10:31:01 (UTC+8)
出版者:	淡江大學
摘要:	The bonding of an S45C steel inserted into copper during cast welding and heat treatment was examined. The interface shear strength was made with a push-out test. After cast welding, a cast-welding layer formed between steel and copper. After marquenching, martempering and austempering heat treatment, there was a cast-welding layer near the steel matrix, an irregular layer near the copper matrix and between of them was a middle layer. Through X-ray diffraction analysis was used to determine that the interface layer consisted of carbon and CuFeO2. Through electron probe X-ray microanalysis (EPMA), it was showed that iron atoms and carbons, mostly, diffused into the copper matrix. The interface shear strengths of the compound casting while with marquenching, martempering, and austempering were 6.29 MPa, 8.23 MPa, and 8.33 MPa, respectively; The fractured region was all happened near S45C steel matrix in the cast welding layer.
關聯:	淡江理工學刊=Tamkang journal of science and engineering 6(1)，頁49-56
DOI:	10.6180/jase.2003.6.1.07
显示于类别:	[機械與機電工程學系暨研究所] 期刊論文

文件中的档案:

档案	描述	大小	格式	浏览次数
1560-6686_6-1-7.pdf		983Kb	Adobe PDF	456	检视/开启
index.html		0Kb	HTML	35	检视/开启

在機構典藏中所有的数据项都受到原著作权保护.

TAIR相关文章