    題名: Novel UV-curable and alkali-soluble resins for light-shielding black matrix application
    作者: Kuo, Kuo-huai;Chiu, Wen-yen;Hsieh, Kuo-huang;董崇民;Don, Trong-ming
    貢獻者: 淡江大學化學工程與材料工程學系
    關鍵詞: Carbon black;UV-curable and alkali-soluble resins;Black matrix;UV-lithography
    日期: 2009-02-01
    上傳時間: 2010-08-09 18:23:02 (UTC+8)
    出版者: Elsevier
    摘要: A carbon black (CB) photo resist, comprising CB, CB dispersant, photo-curable resin, photo-initiator, and solvent, has been developed in order to prepare a light-shielding black matrix (BM) in the liquid crystal display application. In order to prepare a BM with a high opacity property or optical density (OD), the effect of CB such as its particle and concentration on light absorption property was first evaluated, and the results showed that 45 wt% CB with a particle size of about 100 nm in BM could reach an OD value of 4 μm−1. Moreover, six different UV-curable and alkali-soluble resins (A1, A2, and A3; B1, B2, and B3) were synthesized as photo-curable resins. Structures of these resins were characterized by FTIR and GPC, in which concentrations of various functional groups, especially carboxylic acid and double bond, were calculated. Subsequently, their photo-initiated polymerization rate with or without CB were measured. Finally, it was found that through a proper selection of the newly synthesized resins to prepare a carbon black photo resist, a BM with an OD of 4 μm−1 and a good resolution of 10 μm was successfully prepared upon low UV irradiation energy of 50 mJ/cm2.
    關聯: European Polymer Journal 45(2), pp.474-484
    DOI: 10.1016/j.eurpolymj.2008.10.044
    顯示於類別:[化學工程與材料工程學系暨研究所] 期刊論文

    文件中的檔案:

    檔案 大小格式瀏覽次數
    0014-3057_45(2)p474-484.pdf1122KbAdobe PDF401檢視/開啟

    在機構典藏中所有的資料項目都受到原著作權保護.

    TAIR相關文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - 回饋