    題名: Preparation of organic-inorganic nano-composites for antireflection coatings
    作者: Chen, Ching-chung;Lin, Dar-jong;Don, Trong-min;Huang, Feng-hsi;Cheng, Liao-ping
    貢獻者: 淡江大學化學工程與材料工程學系
    關鍵詞: Nano-composites
    日期: 2008-08
    上傳時間: 2010-08-09 18:02:02 (UTC+8)
    出版者: Amsterdam: Elsevier BV * North-Holland
    摘要: In this research, bi-layer thin film stacks that served as an antireflective coating were developed. The top layer was synthesized using tetraethoxysilane and 3-(trimethoxysilyl) propyl methacrylate by the well-known sol–gel technique. Its refractive index was lower than that of the bottom layer, which was prepared by reaction between tetrabutoxyltitanium and γ-glycidoxy propyl trimethoxysilane. Antireflective coatings were obtained by spin-coating of the synthesized sols on a glass substrate, followed by pre-drying, UV-curing, and post-baking. Fourier transform infrared spectrometer was employed to investigate the evolution of chemical bonds during the UV-curing and the sol–gel processes. The size of the inorganic/organic hybrid particles in the sol was found to be less than 10 nm, as measured by transmission electron microscope and dynamic light scattering. Thermo gravimetric analyzer was used to find out the thermal degradation temperature of the two layers and the effect of post-baking. The results indicated that the thermal stability increased after post-baking at 200 °C for 15 min. The reflectance of the antireflection coating was controlled by the relative refractive indices and the thickness of the top and bottom layers. Under optimal synthesis condition, we obtained an antireflection coating, exhibiting a low reflection, 1% at 550 nm, in the visible range.
    關聯: Journal of Non-Crystalline Solids 354(32), pp. 3828-3835
    DOI: 10.1016/j.jnoncrysol.2008.04.010
    顯示於類別:[化學工程與材料工程學系暨研究所] 期刊論文

    文件中的檔案:

    檔案 大小格式瀏覽次數
    0022-3093_354(32)p3828-3835.pdf1048KbAdobe PDF332檢視/開啟

    在機構典藏中所有的資料項目都受到原著作權保護.

    TAIR相關文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - 回饋