    題名: UV-curable PDMS-containing PU system for hydrophobic textile surface treatment
    作者: Chen, Wei-hung;Chen, Po-cheng;Wang, Shih-chieh;Yeh, Jen-taut;Huang, Chi-yuan;Chen, Kan-nan
    貢獻者: 淡江大學化學學系
    關鍵詞: PDMS;UV-curable;PU;Textile;Coating
    日期: 2009-09
    上傳時間: 2010-08-09 16:23:26 (UTC+8)
    出版者: Dordrecht: Springer Netherlands
    摘要: Polydimethylsiloxane (PDMS) is a super-hydrophobic material with low surface energy. UV-curable PDMS-containing polyurethane (PU) oligomer (UV-PDMS-PU), having a PDMS moiety is designed for textile (PET and Nylon) surface treatment with a long lasting hydrophobic property. UV-PDMS-PU was prepared by an addition of 2-hydroxyethyl methacrylate (2-HEMA) to NCO-terminated PDMS-containing PU pre-polymer (NCO-PDMS-PU). NCO-PDMS-PU was obtained from an addition reaction of alkyl hydroxyl-terminated PDMS with an excess amount of isophorone diisocyanate (IPDI). UV-PDMS-PU system consisted of 1% (w/w) photo-initiator that was coated either on glass plate or textile and then cured by UV-radiation. The UV-cured PDMS-containing PU films were evaluated by the measurements of thermal and physical properties. The hydrophobic characters and silicone content were remained on textile surface after water washing cycles, which indicating that UV-curing process can help the PDMS moiety to anchor onto textile fibers.
    關聯: Journal of Polymer Research 16(5), pp.601-610
    DOI: 10.1007/s10965-008-9265-4
    顯示於類別:[化學學系暨研究所] 期刊論文


    檔案 描述 大小格式瀏覽次數
    1022-9760_16(5)p601-610.pdf558KbAdobe PDF477檢視/開啟
    UV-curable PDMS-containing PU system for hydrophobic textile surface treatment.pdf558KbAdobe PDF5檢視/開啟



    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - 回饋