Microstructure of A380–SiC(p) composites for die casting

doi:10.1016/S0924-0136(98)00226-X

淡江大學機構典藏 > 工學院 > 機械與機電工程學系暨研究所 > 期刊論文 > Item 987654321/45821

請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/45821

題名:	Microstructure of A380–SiC(p) composites for die casting
作者:	Lin, C. B.;Ma, C. L.;Chung, Y. W.
貢獻者:	淡江大學機械與機電工程學系
關鍵詞:	Die casting;Particulate metal matrix composite;Microstructure;Segregation
日期:	1998-12
上傳時間:	2010-03-26 20:01:35 (UTC+8)
出版者:	Elsevier
摘要:	The distribution of silicon carbide (SiC) particulate in the matrix of an A380–SiC(p) composite of a die-cast chain wheel depends upon the size of the SiC particulate, the core pin materials and the plunger velocity during the die-casting process. SiC particulate (13 μm) is distributed homogeneously in the die-cast product and the particulate content remains the same after the casting process. However, the 60 μm SiC particulate causes particulate segregation and settling in the shot biscuit and does not pass easily through a gate of 1.0 mm thickness. Further, it reduces the particulate content in the die-cast product and causes inhomogeneous particulate distribution in the teeth of the chain wheel. Using SKH 4A steel as a core pin, the SiC particulate was distributed very uniformly around the screw bolt holes of the product. In contrast, SiC-free zones were observed around the screw bolt holes when using sintered tungsten carbide (WC) as a core pin. A faster plunger velocity of 3.8 m s−1 or a slower velocity of 0.3 m s−1 result in some SiC-free zones in the cast product.
關聯:	Journal of materials processing technology 84(1-3), pp.236-246
DOI:	10.1016/S0924-0136(98)00226-X
顯示於類別:	[機械與機電工程學系暨研究所] 期刊論文

文件中的檔案:

檔案	大小	格式	瀏覽次數
	0Kb	Unknown	270	檢視/開啟
index.html	0Kb	HTML	38	檢視/開啟
Microstructure of A380–SiC(p) composites for die casting.pdf	4179Kb	Adobe PDF	1	檢視/開啟

在機構典藏中所有的資料項目都受到原著作權保護.

TAIR相關文章

資料載入中.....