Studies on the Degradation Behavior of Chitosan-g-Poly (acrylic acid) Copolymers

淡江大學機構典藏 > 工學院 > 化學工程與材料工程學系暨研究所 > 期刊論文 > Item 987654321/44383

請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/44383

題名:	Studies on the Degradation Behavior of Chitosan-g-Poly (acrylic acid) Copolymers
作者:	董崇民;Don, Trong-ming;Chuang, Chung-yang;Chiu, Wen-yen
貢獻者:	淡江大學化學工程與材料工程學系
關鍵詞:	Chitosan;Poly(acrylic acid);Graft Copolymer;Degradation;Lysozyme, Slurry
日期:	2002-12-02
上傳時間:	2010-03-09 10:16:55 (UTC+8)
出版者:	淡江大學
摘要:	Graft copolymers of Chitosan and poly(acrylic acid) were synthesized with a redox initiator, cerium ammonium nitrate. After 2 h of reaction at 70 oC, a gel product was obtained. The swelling ratio of the copolymer in water depends on the pH value and has a maximum in the buffer solution at pH 7. This is because the morphological structure of the copolymers in the water changes with the pH values. In addition, the swelling ratio of the copolymer increases with the feeding amount of acrylic acid monomer. The degradation behavior of the copolymers was observed both in a lysozyme solution and an active slurry solution. The degradation rate was higher in the lysozyme solution and depended on the composition of the copolymers.
關聯:	淡江理工學刊=Tamkang journal of science and engineering 5(4), p.235-240
DOI:	10.6180/jase.2002.5.4.06
顯示於類別:	[化學工程與材料工程學系暨研究所] 期刊論文