Thermochemical behavior of metallic citrate precursors for the production of pure LaAlO3

doi:10.1016/j.jpcs.2008.10.005

淡江大學機構典藏 > 工學院 > 化學工程與材料工程學系暨研究所 > 期刊論文 > Item 987654321/44186

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/44186

题名:	Thermochemical behavior of metallic citrate precursors for the production of pure LaAlO3
作者:	余宣賦;Yu, Hsuan-fu;Wang, Juy;Wang, Shuen-shian;Kuo, Yu-man
贡献者:	淡江大學化學工程與材料工程學系
关键词:	A. Ceramics;B. Chemical synthesis;C. Infrared spectroscopy;C. X-ray diffraction;D. Phase transitions
日期:	2009-01
上传时间:	2010-08-10 10:41:13 (UTC+8)
出版者:	Kidlington: Pergamon
摘要:	Pure LaAlO3 nanoparticles were synthesized, using a citrate-precursor technique. La(NO3)3, Al(NO3)3, and C3H4(OH)(COOH)3, in a molar ratio of 1:1:4.5, were dissolved in deionized water. The pH of the aqueous solution was adjusted using NH4OH. After drying, the citrate precursors were charred at 350 °C, followed by calcination at different temperatures. The thermochemical behavior of the charred citrate precursor to form LaAlO3 was investigated using X-ray diffractometry, infrared spectroscopy, thermogravimetric analysis, and differential thermal analysis. While the charred specimen obtained at pH=2 (without NH4OH addition) was composed of LaAl(OOCH2)3, the charred specimens obtained at pH>2 were composed of LaAlO3−x−y(CO3)x(OH)2y. All these metallic salts were decomposed at temperatures between 600 and 780 °C to form crystalline LaAlO3 but calcining the specimens in air at 800 °C were required to remove all residual chars to produce pure LaAlO3. At 900 °C, the citrate-derived particles obtained at pH>2 were composed of LaAlO3 crystallites with an average size of 30 nm.
關聯:	Journal of Physics and Chemistry of Solids 70(1), pp.218-223
DOI:	10.1016/j.jpcs.2008.10.005
显示于类别:	[化學工程與材料工程學系暨研究所] 期刊論文

文件中的档案:

档案	大小	格式	浏览次数
0022-3697_70(1)p218-223.pdf	662Kb	Adobe PDF	315	检视/开启

在機構典藏中所有的数据项都受到原著作权保护.

TAIR相关文章

数据加载中.....