Photocatalytic abilities of gel-derived P-doped TiO2

doi:10.1016/j.jpcs.2007.01.050

淡江大學機構典藏 > 工學院 > 化學工程與材料工程學系暨研究所 > 期刊論文 > Item 987654321/44185

請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/44185

題名:	Photocatalytic abilities of gel-derived P-doped TiO2
作者:	Yu, Hsuan-Fu
貢獻者:	淡江大學化學工程與材料工程學系
關鍵詞:	A. Ceramics;A. Semiconductors;B. Chemical synthesis;C. X-ray diffraction;D. Phase transitions
日期:	2007-04
上傳時間:	2013-06-13 11:28:47 (UTC+8)
出版者:	Kidlington: Pergamon
摘要:	P-doped TiO2 nanoparticles were synthesized through hydrolysis and condensation of Ti(OC2H5)4 with H3PO4 additions. Effects of [H3PO4]/[Ti(OC2H5)4] molar ratios on the anatase-to-rutile phase transformation, crystallite sizes, surface areas, and photocatalytic abilities of the gel-derived P-doped TiO2 were investigated. The P-doped TiO2 nanoparticles prepared by [H3PO4]/[Ti(OC2H5)4]=0.03 were composed of anatase monophase even at 900 oC and possessed very strong photocatalytic ability. Kinetic studies on the P-doped TiO2 to photocatalytically decompose methylene blue under irradiation of 365 nm UV light found that the P-doped TiO2 prepared by [H3PO4]/[Ti(OC2H5)4]=0.03 and calcined at 800 oC had the specific reaction rates, at 25 °C, kA,m=0.76 m3/(kg min) (based on the mass of P-doped TiO2) and kA,BET=46.2×10−6 m/min (based on the BET surface area of P-doped TiO2), which is superior to the performance of a commercial product, P25 (kA,m=0.22 m3/(kg min) and kA,BET=4.8×10−6 m/min).
關聯:	Journal of Physics and Chemistry of Solids 68(4), pp.600-607
DOI:	10.1016/j.jpcs.2007.01.050
顯示於類別:	[化學工程與材料工程學系暨研究所] 期刊論文

文件中的檔案:

檔案	描述	大小	格式	瀏覽次數
0022-3697_68(4)p600-607.pdf		298Kb	Adobe PDF	154	檢視/開啟
0022-3697_68(4)p600-607.pdf		298Kb	Adobe PDF	1	檢視/開啟

在機構典藏中所有的資料項目都受到原著作權保護.

TAIR相關文章

資料載入中.....