    题名: 聚乙烯醇接枝玉米澱粉與PHB摻合體的製備與性質
    其它题名: Preparation and characterization of poly(vinylalcohol)-g-starch blended with PHB
    作者: 商瑋薇;Shang, Wei-wei
    贡献者: 淡江大學化學工程與材料工程學系碩士班
    董崇民;Don, Trong-ming
    关键词: 聚羥基丁酯;玉米澱粉;聚乙烯醇;PHB;corn starch;PVA
    日期: 2006
    上传时间: 2010-01-11 05:37:03 (UTC+8)
    摘要: 因為PHB價格過高,於是藉著摻合同樣具有生物可分解性但價格便宜的澱粉來降低成本。而為了增加澱粉和PHB的相容性,於是將和PHB相容的PVAc接枝到澱粉上,所製備出的PHB/PVAc-starch摻合體不僅具有良好的成膜性,而且韌性及熱穩定性都有增加。本研究進一步將PVAc鏈段醇化成具有生物可分解性之PVA鏈段,探討PHB和PVA-starch摻合體的結構、性質及酵素水解性。由DSC測試得知不同組成的PHB/CSV摻合體只呈現單一Tg,且Tg隨CSV組成增加而增加,利用Gordon-Taylor方程式可以成功的描述PHB/CSV摻合體的Tg與組成關係(k=0.11)。而經過澱粉酶酵素水解三天後的PHB/CSV摻合體,測試結果為摻合膜中只有澱粉能被酵素攻擊,重量損失隨CSV組成增加而增加,故澱粉水解完全後測得的PHB/CSV摻合膜之Tg,即為PHB/PVAc的玻璃轉移溫度。由TGA測試結果得知PHB/CSV摻合體呈現三階段熱裂解行為,最大裂解速率隨CSV組成增加而增加,焦炭殘渣量也隨CSV組成增加而增加,可以證明此摻合體的熱穩定性依CSV組成增加而有所提升。再將CSV醇解成CSA,利用FTIR進行結構分析後與PHB進行摻合,由DSC測試得知PHB/CSA摻合體為一部份相容系統,個別呈現PHB及CSA的Tg。PHB/CSV摻合體呈現出三階段的裂解行為,同時起始裂解溫度隨CSA組成增加而下降。而由DSC圖中可知,當將裝有PHB/CSA摻合體的鋁盤置於220oC加熱台中熔融1分鐘,PHB已產生裂解,故摻合體中PHB成分之Tg及Tm隨CSA組成增加而降低。至於PHB/CSA摻合體之酵素水解結果與PHB/CSV摻合體相差不大,證明澱粉酶對澱粉的專一性。
    In order to reduce the PHB cost to blend with that have biodegradable starch. So as to do increase the miscibility between PHB and starch, vinyl acetate monomer was graft polymerized onto starch with a redox initiator, cerium ammonium nitrate (CAN). PHB/PVAc-starch have good film to increase toughness and thermalstability. In this study, alcoholize PVAc chain to PVA chain, to discuss structure, properties and endymatic hydrolysis of PHB/PVA-starch. The composition prepared in this research are as follows: PHB/CSV =10/0, 9/1, 7/3 , 5/5 , 3/7, 1/9, 0/10(CSV is the reaction product and its grafting ratio is 0.27). Thermal degradation behavior was analyzed by thermal gravimetric analysis, the glass transition temperature Tg and the degree of crystallization of the blends were observed by differential scanning calorimetry and their morphology were characterized by the scanning electron microscopy.