淡江大學機構典藏:Item 987654321/32747
English  |  正體中文  |  简体中文  |  Items with full text/Total items : 58605/92268 (64%)
Visitors : 540351      Online Users : 68
RC Version 7.0 © Powered By DSPACE, MIT. Enhanced by NTU Library & TKU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
  • Adv. Search
    HomeLoginUploadHelpAboutAdminister Goto mobile version
    Please use this identifier to cite or link to this item: http://tkuir.lib.tku.edu.tw:8080/dspace/handle/987654321/32747


    Title: (R0.5A0.5)BO3 (R = Gd, Yb;A = Ca, Sr;B = Mn, Ti or A = Ce, Th;B = Ni)氧化物的結構與特性研究
    Other Titles: Structure and properties of (R0.5A0.5)BO3 (R = Gd, Yb;A = Ca, Sr;B = Mn, Ti or A = Ce, Th;B = Ni) oxides
    Authors: 陳俊瑋;Chen, Chun-wei
    Contributors: 淡江大學化學學系碩士班
    高惠春;Kao, Huey-chuen I.
    Keywords: 鈣鈦礦;巨磁阻;檸檬酸鹽先驅物法;錳氧化物;perovskite;Magnetoresistance;citrate method
    Date: 2005
    Issue Date: 2010-01-11 02:41:02 (UTC+8)
    Abstract: 本研究使用聚合的檸檬酸鹽先驅物法製備(R0.5A0.5)MnO3(R = Gd, Yb; A = Ca, Sr)與(R0.5A0.5)NiO3(A = Ce, Th)樣品,使用固態法製備(R0.5A0.5)TiO3 (A = Ca, Sr)。(R0.5A0.5)MnO3系列為正交晶系;(R0.5A0.5)NiO3系列為單斜晶系。SEM圖譜顯示利用檸檬酸鹽先驅物法製備的樣品,都具有較好的均勻度,而且樣品顆粒半徑較小。經由固態法製備的樣品則粒徑較大。經由XANES光譜判定Mn及Ti都具有3價與4價的混合價數。(R0.5A0.5)MnO3系列樣品皆為絕緣態,並具有類似自旋玻璃態的性質,FC與ZFC之變溫磁化率呈現不可逆的現象。所有樣品皆有負磁阻,且爐冷樣品的磁阻較驟冷樣品為高。(R0.5A0.5)MnO3系列樣品之磁阻值在80-100 K時約為60-65%。(R0.5A0.5)NiO3系列樣品呈現順磁金屬性,最大磁阻值溫度在200 K左右,約在50-60%。(R0.5A0.5)TiO3系列樣品為順磁性,並為Mott絕緣體。
    In this research, homogeneous (R0.5A0.5)MnO3 (R = Gd, Yb; A = Ca, Sr) and (R0.5A0.5)NiO3 (A = Ce, Th) compounds with perovskite structure were synthesized by a polymeric citrate precursor method. (R0.5A0.5)TiO3 (A = Ca, Sr) was synthesized by a solid state method. (R0.5A0.5)MnO3 series samples have orthorhombic symmetry and (R0.5A0.5)NiO3 have monoclinic symmetry. The samples prepared by the polymeric citrate precursor method has a better homogeneity and the grain size is smaller than that prepared by the solid state method. Mn and Ti samples have M3+ and M4+ mixed valence state observed by XANES. The (R0.5A0.5)MnO3 samples are insulator, they has a spin-glass like property and the FC and ZFC susceptibility is irreversible. The (R0.5A0.5)NiO3 samples are paramagnetic metal. At 1 T magnetic field, both (R0.5A0.5)MnO3 and (R0.5A0.5)NiO3 have negative magnetoresistance (MR) ratio. The maximum MR ratio of (Gd0.5Ca0.5)MnO3 sample is found at 80-100 K,with a range of 60-65%. The maximum MR ratio of (R0.5A0.5)NiO3 sample is found at 180-200 K, with a range of 50- 60%. The (R0.5A0.5)TiO3 samples are paramagnetic Mott insulator.
    Appears in Collections:[Graduate Institute & Department of Chemistry] Thesis

    Files in This Item:

    File SizeFormat
    0KbUnknown470View/Open

    All items in 機構典藏 are protected by copyright, with all rights reserved.


    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - Feedback