淡江大學機構典藏:Item 987654321/32677
English  |  正體中文  |  简体中文  |  Items with full text/Total items : 64191/96979 (66%)
Visitors : 8408205      Online Users : 7833
RC Version 7.0 © Powered By DSPACE, MIT. Enhanced by NTU Library & TKU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
    •  Adv. Search
    Home ‧ Login ‧ Upload ‧ Help ‧ About ‧ Administer Goto mobile version


    Please use this identifier to cite or link to this item: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/32677


    Title: (Gd2-yMy)Ti2O7-y/2 (M = Ca, Sr)結構參數變化的研究
    Other Titles: Structure parameters of (Gd2-yMy)Ti2O7-y/2 (M = Ca, Sr)
    Authors: 劉學明;Liu, Hsueh-ming
    Contributors: 淡江大學化學學系碩士班
    高惠春;Kao, Huey-chuen I.
    Keywords: (Gd2-yMy)Ti2O7-y/2;焦綠石;晶格參數;聚合多質子酸先驅物法;XANES;(Gd2-yMy)Ti2O7-y/2;pyrochlore;lattice parameters;polymeric citrate precursor method;XANES
    Date: 2008
    Issue Date: 2010-01-11 02:32:43 (UTC+8)
    Abstract: 本研究使用聚合多質子酸先驅物法於不同溫度800 ~ 1400 oC下製備(Gd2-yMy)Ti2O7-y/2 (M = Ca, Sr; y = 0.050, 0.100)樣品，當燒結溫度為800 ~ 1400 oC時皆為焦綠石的結構，其空間群為Fd3m。樣品粒徑大小根據SEM圖中顯示大約為400 ~ 800 nm，緻密度為50 ~ 65%。隨燒結溫度的上升，單位晶胞a-軸的長度逐漸變大，長度為10.192(1) < a < 10.209(1) Å。Gd-O(1)和Ti-O(3)鍵長相同約為2.21(1) Å；Gd-O(2)鍵長較長約為2.52(1) Å；而Ti-O(2)鍵長相對較短約為1.97(1) Å。O(3)位置之佔有率也隨溫度升高而增加，使O(2)位置的x座標(fractional coordinate)受到O(3)位置的擠壓而有變大的趨勢。本系列樣品中Ti的價數經由XANES光譜的測量，推測沒有混價情形發生，為四價金屬離子。
    Four samples with nominal compositions of (Gd2-yMy)Ti2O7-y/2 (M = Ca, Sr; y = 0.050, 0.100) were prepared with different temperatures from 700 - 1400 oC by a polymeric citrate precursor method. Pyrochlore phase with a space group of Fd3m was observed for all the samples except for those prepared at 700 oC. Particle size of (Gd2-yMy)Ti2O7-y/2 compounds are about 400 - 800 nm observed under SEM. Relative density of these samples are in the range of 50 - 65%. Unit cell a-axis (ea. 10.192(1) - 10.209(1) Å) and occupancy of the O(3) site (ea. 1 - 8%) increase with increasing the preparation temperature. Gd−O(1) and Ti−O(3) have the same bond length. They are about 2.21(1) Å. Gd−O(2) has a longer bond length, that is 2.52(1) Å. On the other hand, Ti−O(2) has a shorter bond length, that is about 1.97(1) Å. Increasing occupation factor of the O(3) site would increase the x fractional coordinate of the O(2) site. Ti L-edge XANES spectra show that all the samples have Ti(IV) valence state.
    Appears in Collections:[Graduate Institute & Department of Chemistry] Thesis

    Files in This Item:

    File SizeFormat
    0KbUnknown522View/Open

    All items in 機構典藏 are protected by copyright, with all rights reserved.

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - Feedback