Selective area growth of carbon nanostructure synthesized by catalyst-assisted conversion of nanodiamond films

doi:10.1016/j.diamond.2004.10.022

淡江大學機構典藏 > 理學院 > 物理學系暨研究所 > 期刊論文 > Item 987654321/27468

請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/27468

題名:	Selective area growth of carbon nanostructure synthesized by catalyst-assisted conversion of nanodiamond films
作者:	Teng, Mao-ying;Liu, Kuo-shung;Lee, Yen-chih;Lin, Sue-chun;Cheng, Hsiu-fung;林諭男;Lin, I-nan
貢獻者:	淡江大學物理學系
關鍵詞:	Nanodiamonds;Carbon materials;Electron field emission
日期:	2005-03-01
上傳時間:	2009-12-31 10:10:41 (UTC+8)
出版者:	Elsevier
摘要:	The electron field emission properties of carbon nanotubes (CNTs) formed by catalyst-assisted solid-state growth process from nanodiamond films were investigated. The SEM and Raman spectroscopy examinations show that the nanodiamond films were converted into carbon nanotubes when they were coated with a thin layer of Fe, Co or Ni films (∼1.0 nm) and then postannealed at high enough temperature (∼1000 °C). Precoating a catalytic metal layer is of prime importance to induce the phase transformation process. The field emission properties of nanodiamond films have been dramatically improved. The turn on field was reduced from EDia=36–44 V/μm for nanodiamond films to ECNTs=11 to 16 V/μm, whereas the electron field emission capacity was increased from Je(Dia)=110 μA/cm2 for nanodiamond films to Je(CNTS)=30 mA/cm2 after the conversion process. The electron field emission of the solid-state converted CNTs thus obtained are superior to those of the CNTs grown from CVD process due to the suppression of carbon soots formation.
關聯:	Diamond and Related Materials 14(3-7), pp.825-830
DOI:	10.1016/j.diamond.2004.10.022