The peritectic transition of Bi-2223 superconductor with TG and DTA

淡江大學機構典藏 > 工學院 > 化學工程與材料工程學系暨研究所 > 期刊論文 > Item 987654321/25363

請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/25363

題名:	The peritectic transition of Bi-2223 superconductor with TG and DTA
其他題名:	以TG和DTA研究Bi-2223超導體的包晶轉變
作者:	Yin, S. C.;Wei, T. P.;Wang, C. M.;Kao, H. C. I.
貢獻者:	淡江大學化學學系
日期:	1996-03-01
上傳時間:	2009-12-01
出版者:	New York: Springer New York LLC
摘要:	Peritectic transition of a Bi-2223 superconductor was studied with TG and DTA under different heating rate (R, °C/min) and oxygen partial pressures. Linear relationships were observed between Tp (peritectic transition temperature) vs. R, and weight loss (equivalent to the O-atom loss per mole) vs. R under 25 mL/min in flowing 1% O2 partial pressure. Extrapolated to infinite rate, 0°C/min, Tp was 821 °C found from the peak temperature of the DTA curves, and 1.49 O-atom loss. Increasing oxygen partial pressure, Tp was increased but the weight loss was decreased. About 60°C difference in Tp was found between 1 and 100% of partial oxygen pressure under 10°C/min heating rate. Only 0.26 O-atom loss was observed under 100% oxygen partial pressure. Stability of Bi-2223 superconductor around its peritectic point was greatly enhanced by increasing the oxygen partial pressure.
關聯:	Czechoslovak Journal of Physics 46, supp.3, pp.1499-1500