    題名: Self-curable aqueous polymeric dyes for printing and dyeing applications
    作者: Chen, Kan-nan;Huang, Ching-tzer
    貢獻者: 淡江大學化學學系
    關鍵詞: self-curable;polymeric dye;aqueous epoxy resin
    日期: 2006-05-05
    上傳時間: 2009-11-04 16:55:31 (UTC+8)
    出版者: John Wiley & Sons
    摘要: An epoxy resin (NPES-904, epoxy equivalent weight is 815) with a repeating unit, n > 4 was selected as a polymer backbone of polymeric dye. Water-reducible epoxy resin was prepared by a semiesterification of its secondary hydroxy group with succinic anhydride and then dispersed to aqueous phase after it was neutralized with triethylamine. An aqueous polymeric dye was obtained from a ring opening reaction of that epoxy resin with amino group of a direct dye (soluble dye such as C. I. Acid Blue 62, C. I. Direct Orange 39 or C. I. Direct Red 2). These aqueous polymeric dye dispersions carried the average particle sizes between 50 and 90 nm. A polyaziridine was added as a latent curing agent and forming a self-curable system of aqueous polymeric dye solution, which was stable in aqueous phase when its pH remained above 8.0. This aqueous polymeric dye was self-cured on drying at ambient temperature and results in the formation of waterproof and solvent-resistant polymeric dye. These self-curable polymeric dyes had potential for jet ink printing and dyeing applications.
    關聯: Journal of Applied Polymer Science 100(3), pp.1919-1931
    DOI: 10.1002/app.22517
    顯示於類別:[化學工程與材料工程學系暨研究所] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    0021-8995_100(3)p1919-1931.pdf240KbAdobe PDF271檢視/開啟

    在機構典藏中所有的資料項目都受到原著作權保護.

    TAIR相關文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - 回饋