    題名: The permeation resistance of polyethylene, polyethylene/polyamide and polyethylene/modified polyamide blown tubes against unleaded gasoline
    作者: Yeh, Jen-taut;Chang, Sheng-shan;Yao, Hung-tse;Chen, Kan-nan;Jou, Wern-shiarng
    貢獻者: 淡江大學化學學系
    日期: 2000-03-01
    上傳時間: 2009-11-04 16:52:42 (UTC+8)
    出版者: Springer
    摘要: The barrier resistance of polyethylene (PE), polyethylene/polyamide (PE/PA) and polyethylene/modified polyamide (PE/MPA) blown tubes against gasoline permeation is reported. The blown tubes prepared from pure PE exhibited much poorer gasoline permeation resistance than PE/PA and PE/MPA blown tubes. About 93% of the filled gasoline permeated out of PE blown tubes in 14 days at 40�C. In contrast, the gasoline permeation resistance of the blown tubes improved significantly by blending MPA (or PA) before tube blowing. PE/MPA blown tubes exhibited significantly better gasoline permeation resistance than PE/PA blown tubes of the same PE contents. The order of gasoline permeation resistance of PE/MPA blown tubes is the same as the order of the barrier resistance of MPA resins against gasoline permeation before blending with PE. In fact, by using proper compositions and carefully controlling the MPA morphology, the gasoline permeation resistance of the PE/MPA blown tubes can reach about 360 times better than that of pure PE blown tubes at 25�C. These interesting phenomena were investigated in terms of the morphology, thermal and rheological properties of the base resins and/or blown tubes of PE/PA and PE/MPA blends.
    關聯: Journal of Materials Science 35(6), pp.1321-1330
    DOI: 10.1023/A:1004761520144
    顯示於類別:[化學工程與材料工程學系暨研究所] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    0022-2461_35(6)p1321-1330.pdf857KbAdobe PDF332檢視/開啟

    在機構典藏中所有的資料項目都受到原著作權保護.

    TAIR相關文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - 回饋