Preparation and characterization of H3PW12O40/ZrO2 catalyst for carbonation of methanol into dimethyl carbonate

doi:10.1007/s11164-018-3383-3

淡江大學機構典藏 > 工學院 > 化學工程與材料工程學系暨研究所 > 期刊論文 > Item 987654321/127397

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: https://tkuir.lib.tku.edu.tw/dspace/handle/987654321/127397

题名:	Preparation and characterization of H3PW12O40/ZrO2 catalyst for carbonation of methanol into dimethyl carbonate
作者:	Chao Lung Chiang, Kuen Song Lin, Ssu-Han Yu
关键词:	Carbon dioxide, Methanol Carbonation, Dimethyl carbonate, H3PW12O40/ZrO2 catalyst, Greenhouse effect gas
日期:	2018-03-15
上传时间:	2025-06-04 12:05:29 (UTC+8)
出版者:	Springer
摘要:	A H3PW12O40/ZrO2 catalyst for effective dimethyl carbonate (DMC) formation via methanol carbonation was prepared using the sol–gel method. X-ray photoelectron spectra showed that reactive and dominant (63%) W(VI) species, in WO3 or H2WO4, enhanced the catalytic performances of the supported ZrO2. The mesoporous structure of H3PW12O40/ZrO2 was identified by nitrogen adsorption–desorption isotherms. In particular, partial sintering of catalyst particles in the duration of methanol carbonation caused a decrease in the Brunauer–Emmett–Teller surface area of the catalyst from 39 to 19 m2/g. The strong acidity of H3PW12O40/ZrO2 was confirmed by the desorption peak observed at 415 °C in NH3 temperature-programmed desorption curve. At various reaction temperatures (T = 110, 170, and 220 °C) and CO2/N2 volumetric flow rate ratios (CO2/N2 = 1/4, 1/7, and 1/9), the calculated catalytic performances showed that the optimal methanol conversion, DMC selectivity, and DMC yield were 4.45, 89.93, and 4.00%, respectively, when T = 170 °C and CO2/N2 = 1/7. Furthermore, linear regression of the pseudo-first-order model and Arrhenius equation deduced the optimal rate constant (4.24 × 10−3 min−1) and activation energy (Ea = 15.54 kJ/mol) at 170 °C with CO2/N2 = 1/7 which were favorable for DMC formation.
關聯:	Research on Chemical Intermediates, 44, p.3797-3811
DOI:	10.1007/s11164-018-3383-3
显示于类别:	[化學工程與材料工程學系暨研究所] 期刊論文