题名:	Microstructural evaluation of interfacial intermetallic compounds between Sn58Bi and ENEPIG
作者:	Wang, Yi-wun;Tsai, Cheng-ting;Fang, Jang-cheng;Lin, Tzu-yi
日期:	2024-04-17
上传时间:	2024-07-31 12:10:00 (UTC+8)
出版者:	ELSEVIER
摘要:	Background Low carbonization and Restriction of Hazardous Substances (RoHS) regulations have promoted the development of low-temperature lead-free solder. The solder and substrate are critical entities of joint connections. Methods Sn58Bi has been considered a promising low-temperature solder. Electroless nickel/electroless palladium/immersion gold (ENEPIG) is a good surface finish that prevents solder joints from oxidizing and extends the shelf life of the substrates. In this study, the interfacial reactions between the Sn58Bi solder and ENEPIG surface finish were systematically analyzed. Findings (Au,Pd,Ni)(Sn,Bi)4 was observed after reflow at 160 °C. Au and Pd dissolved into solder rapidly in the beginning. NiSn4 and Ni3Sn4 with small amounts of Au and Pd dissolution formed at the interface after aging. The morphology of NiSn4 evolved from block-like to needle-shaped and finally to a layered configuration as the aging temperature and time increase. Ni3Sn4 was observed between NiSn4 and substrate above 100 °C. This study established the growth mechanism of intermetallic compounds (IMCs) in the reaction between Sn58Bi and ENEPIG for low-carbon emitting processes.
關聯:	Journal of the Taiwan Institute of Chemical Engineers 159,　105508
DOI:	10.1016/j.jtice.2024.105508
显示于类别:	[化學工程與材料工程學系暨研究所] 期刊論文

文件中的档案:

档案	描述	大小	格式	浏览次数
index.html		0Kb	HTML	69	检视/开启

在機構典藏中所有的数据项都受到原著作权保护.

TAIR相关文章

数据加载中.....