淡江大學機構典藏:Item 987654321/120956
English  |  正體中文  |  简体中文  |  Items with full text/Total items : 59160/92571 (64%)
Visitors : 739442      Online Users : 37
RC Version 7.0 © Powered By DSPACE, MIT. Enhanced by NTU Library & TKU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
  • Adv. Search
    HomeLoginUploadHelpAboutAdminister Goto mobile version
    Please use this identifier to cite or link to this item: http://tkuir.lib.tku.edu.tw:8080/dspace/handle/987654321/120956


    Title: Enhancing photocatalytic ability of TiO2 films using gel-derived P/Si-TiO2powder
    Authors: Yu, Hsuan-Fu;Cheng, Chao-Wei
    Keywords: TiO2 films;Photocatalysis;Kinetics;Dye degradation;Optical properties;Microstructure
    Date: 2021-01-16
    Issue Date: 2021-08-19 12:13:01 (UTC+8)
    Abstract: P/Si-TiO2 photocatalytic thick films on FTO glass substrates were prepared. TiO2 thin films, as base layer, were first coated on substrates using a spin-coating technique. The slurry containing P/Si-TiO2 nanoparticles was bar-coated on the surface of TiO2 base layer, followed by calcining at 550 °C. The resultant films were characterized using x-ray diffractometer, scanning electron microscope, UV–Vis spectrophotometer, crosscut adhesion test, and recycling-use test. Under 365-nm UV-light irradiation, abilities of the films to photocatalytically degrade methylene blue were evaluated. The apparent rate laws obeyed 1st-order and the corresponding reaction rate constants (k′), based on the coated area of substrates, were estimated. k′ of the thick film (thickness: 6.5 μm; composition: P/Si-TiO2 anatase crystallites with 16 nm average size) was 49.0 L/(m2-sub. h), which was about eight times of that of the thin film (k′ = 6.2 L/(m2-sub. h); thickness: 215 nm; composition: pure TiO2 anatase crystallites with 8-nm average size).
    Relation: Journal of Sol-Gel Science and Technology ,97,p.259–270
    DOI: 10.1007/s10971-020-05450-5
    Appears in Collections:[Graduate Institute & Department of Chemical and Materials Engineering] Journal Article

    Files in This Item:

    File Description SizeFormat
    index.html0KbHTML28View/Open

    All items in 機構典藏 are protected by copyright, with all rights reserved.


    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library & TKU Library IR teams. Copyright ©   - Feedback