题名:	Enhanced electrochromic performance of carbon-coated V2O5 derived from a metal–organic framework
作者:	Hsiao, Yu-Sheng;Cai-Wan, Chang-Jian;Syu, Wei-Lin;Yen, Shih-Chieh;Huang, Jen-Hsien;Weng, Huei-Chu;Lu, Cheng-Zhang;Hsu, Shih-Chieh
关键词:	Electrochromism;Metal–organic framework;V2O5;Carbon coating;High conductivity
日期:	2021-03-15
上传时间:	2021-03-12 12:11:03 (UTC+8)
摘要:	In this study we synthesized a vanadium (V)-containing metal–organic framework (MOF) and used it as a template to prepare V2O5 NPs. We used MIL-47, a V-containing MOF having uniform C and V distributions, as a precursor for the preparation of carbon-coated V2O5 (C@V2O5) samples through annealing. The C@V2O5 structures were readily dispersed in poly(3,4-ethylenedioxythiophene):polystyrenesulfonate (PEDOT:PSS) to form stable solutions, allowing the deposition of C@V2O5 on various substrates through simple low-temperature solution-based processes. The uniform coating of carbon on V2O5 was useful for two reasons: (i) the outer layer enhanced the electronic conductivity of a V2O5 electrode and its corresponding electrochemical properties and (ii) based on the electrochemical quartz crystal microbalance (EQCM) analysis, the carbon coating served as a buffer layer that allowed Li+ ion transport, but blocked migration of solvent into the V2O5 electrode, thereby improving the dimensional and electrochemical stability. Compared with the bare V2O5, C@V2O5 exhibited excellent electrochromic (EC) performance, with an EC contrast of 45.8%, a mean response time of 3.4 s, and a coloration efficiency of 89.3 cm2/C. C@V2O5 also displayed higher cycling stability (80.6% retention after 5000 cycles) and highly reversible ionic transport during redox reactions, compared with those of the bare V2O5.
關聯:	Applied Surface Science 542, 148498
DOI:	10.1016/j.apsusc.2020.148498
显示于类别:	[化學工程與材料工程學系暨研究所] 期刊論文

文件中的档案:

档案	描述	大小	格式	浏览次数
index.html		0Kb	HTML	89	检视/开启

在機構典藏中所有的数据项都受到原著作权保护.

TAIR相关文章

数据加载中.....